Solvent-free preparation and thermocompression self-assembly: an exploration of performance improvement strategies for perovskite solar cells

Perovskite solar cells (PSCs) exhibit sufficient technological efficiency and economic competitiveness. However, their poor stability and scalability are crucial factors limiting their rapid development. Therefore, achieving both high efficiency and good stability is an urgent challenge. In addition, the preparation methods for PSCs are currently limited to laboratory-scale methods, so their commercialization requires further research. Effective packaging technology is essential to protect the PSCs from degradation by external environmental factors and ensure their long-term stability. The industrialization of PSCs is also inseparable from the preparation technology of perovskite thin films. This review discusses the solvent-free preparation of PSCs, shedding light on the factors that affect PSC performance and strategies for performance enhancement. Furthermore, this review analyzes the existing simulation techniques that have contributed to a better understanding of the interfacial evolution of PSCs during the packaging process. Finally, the current challenges and possible solutions are highlighted, providing insights to facilitate the development of highly efficient and stable PSC modules to promote their widespread application.


Introduction
Perovskite compounds with a chemical formula ABX 3 have the three-dimensional (3D) crystal structure shown in Fig. 1a. 1 The A-site cations are not thought to contribute directly to the band structure, but they play an important role in maintaining structural stability.This was achieved through charge compensation in the PbI 6 octahedron, which is primarily facilitated by electrostatic (van der Waals) interactions with the inorganic cage. 2,3Methylammonium lead halide (MAPbI 3 ) is a typical perovskite with a simple cubic lattice, in which Pb ions are centered on the octahedron and methylammonium (MA) ions are located between the octahedral building blocks.The most symmetric phase of MAPbI 3 and its related materials is the cubic (Pm3m) lattice, which typically reduces symmetry through an octahedral tilting sequence transformation.The cumulative effect of these tilts leads to a phase transition from cubic to quadrilateral (Fig. 1b and c). 4 Such transformations can alter the electronic band structure, consequently inuencing the photoelectric properties of the material.The size of the A-site cations is a critical factor in this dynamic.Larger cations expand the lattice and reduce the band gap, while smaller cations have the opposite effect.The properties of PSCs can be tailored signicantly via adjusting A-site cations.For example, by adding a cation with a small effective radius (MA + ) to FAPbI 3 , the Goldschmidt tolerance factor can be adjusted to approximately 1. 5 This has been achieved by either shrinking the lattice (Fig. 1d) or relaxing the crystal strain of the FA-based perovskite (Fig. 1e), thereby stabilizing the cubic phase of the perovskite. 68][9] Despite the impressive performance of these devices, the intricate interactions between the perovskite layer and other functional layers can affect their formation and subsequent behavior. 10,11he quest for optimal PSC performance has intensied in recent years, with particular focus on the preparation of highquality perovskite lms and the reduction of chargerecombination losses within the perovskite layer and at the interfaces. 12,13In previous reports, [14][15][16] perovskite microcrystals were mainly obtained by rapid nucleation crystallization in a saturated solution.However, the poor controllability of the nucleation process results in discontinuous microcrystalline lms characterized by rough surfaces and large voids, which do not meet the uniformity and repeatability standards required for large-scale production. 17In addition, the organic hole transport layer (HTL) commonly used in solvent methods is expensive and exhibits poor stability, 18,19 which leads to difficulties in subsequent electrode deposition and device manufacturing.Therefore, exploring deposition technologies suitable for industrial production has become a crucial focus in PSC research.Vapor-deposition methods are a promising solution for large-scale production as they enable the low-cost deposition of stable inorganic HTLs by using vacuumdeposition principles. 20Magnetron sputtering is one of the fastest developing vapor-deposition technologies in the electronics industry and has the advantages of a wide selection of suitable materials, uniform and dense lm formation, and fast deposition. 21Peng et al. prepared uorine-doped tin oxide (FTO)/NiO x /perovskite/SnO 2 /Ag devices by magnetron sputtering and achieved the magnetron-sputtering deposition of all the functional layers of a PSC for the rst time. 22Both magnetron sputtering of the perovskite layer and continuous deposition on the perovskite layer destroy the so lattice of the perovskite. 23A breakthrough in high-quality perovskite deposition via magnetron sputtering was achieved by post-treatment with methyl amine gas. 23,24Furthermore, to prevent potential damage caused by further deposition of SnO 2 , a mixed sputtering buffer layer of polymethacrylate (PMMA) and phenyl-C 61 -butyric acid methyl ester (PCBM) was deposited on the perovskite layer. 22his lm protects the delicate lattice structure of the perovskite and ensures efficient charge transfer within the nal cell.
Widely used conventional solution-based deposition methods present challenges related to solvent compatibility and thermal budget constraints, 25,26 which limit the range of materials and structures that can be effectively applied to devices.Notably, it is challenging to deposit most metal oxides on top of perovskite layers using traditional solvent methods. 27An alternative approach involves the formation of stacked perovskite lms via hot pressing, 28 which effectively avoids solvent compatibility and thermal budget limitations.Lamination processes have emerged as an attractive method for manufacturing PSCs owing to their self-encapsulating nature and compatibility with high-throughput manufacturing methods. 29Furthermore, the pressure applied during processing can enhance the PSC performance by improving the interfacial microstructure between layers. 30,31Fig. 2a illustrates the most successful and widely studied conguration, while Fig. 2b introduces an inverted structure. 11Regardless of the specic conguration, MAPbI 3 is the most typical perovskite for photovoltaic applications.Its superior properties and performance make it a focal point of ongoing efforts to increase the efficiency and stability of PSCs to record levels.
Numerous studies have shown that polycrystalline perovskite lms with large grains have a long carrier diffusion length, high mobility, and high photoluminescence quantum efficiency owing to their high crystal quality, high degree of orientation, low resistance, few grain boundaries, and low number of defects. 33,34However, the loss of organic cations or halide anions during thermal annealing can produce point defects, such as uncoordinated lead ions or halide vacancies.These defects can accelerate PSC degradation during operation under light irradiation and photothermal effects. 35In addition to thermal annealing, the accumulation of ions at the interfaces can initiate slow electrochemical reactions, potentially compromising the selective contact materials and triggering severe degradation. 36ven if the material is properly encapsulated (or measured under laboratory conditions in an inert atmospheres), the device may be unstable.In particular, electric eld-induced ion transport can lead to chemical reactions with external iodide ions. 37,38his review focuses on the strategies for enhancing the performance of PSCs.First, the solvent-free preparation methods for perovskite materials and new techniques for the self-assembly of PSCs are discussed.The factors that degrade the power conversion efficiency (PCE) and stability of PSCs, current techniques employed to address these challenges, and potential avenues for further improvement are explored.This review summarizes the internal and external degradation mechanisms at the device and module levels by analyzing solvent-free methods for preparing perovskite lms, PSC selfassembly methods, and the contact between the layers.Furthermore, existing problems and their potential solutions are proposed.This review provides a new idea for improving the PCE and module stability of PSCs.

Preparation of perovskite active layer by magnetron sputtering
Currently, the predominant deposition technology for perovskite active layer is the solvent method, which is widely recognized as a cost-effective manufacturing process that achieves devices with high PCE. 13,39However, commercial production is difficult with the solvent method as the lm uniformity and repeatability are limited at large scales. 40The inherent difficulty arises from the uncontrollable volatility and uidity of solutions.Solvents with excessively high or low volatility can lead to low perovskite lm quality, resulting in poor photoelectric performance. 41In the solvent method, solvent evaporation inevitably results in the formation of numerous pinholes, which compromise the integrity and stability of the porous lms. 42urthermore, the residual dimethyl sulfoxide and amorphous phase at the interface of the perovskite lm produce harmful cavities aer irradiation, resulting in many nonradiative composite defects. 43In addition, the toxicity of the anti-solvent that needs to be added during the preparation of perovskite precursors is a serious problem. 44More information about the preparation of PSCs using various solvent methods can be found in previous reports. 44,45In contrast, there are many solvent-free methods to prepare perovskite layers, such as vapor deposition, molten salt method, solid phase method and mechanical synthesis.Among them, magnetron sputtering technology is a mature, established, and reproducible method for depositing thin lms that is applicable at both laboratory and industrial scales. 46Besides, at present, there are few researches on the preparation of perovskite active layer by solvent-free method.At present, magnetron sputtering of perovskite active layer can reduce the direct contact between human and perovskite and improve the safety.Therefore, the use of magnetron sputtering for all functional layers can promote the commercialization of PSCs. 22Perovskite lms prepared by magnetron sputtering exhibit enhanced properties, and PSCs fabricated on FTO-coated glass surfaces have promising commercial and industrial applications. 47,48nother important issue is transitioning high-PCE PSC technology from laboratory-scale preparation to commercialscale high-throughput production with minimal PCE loss.Magnetron sputtering technology has the characteristics of low cost, high object utilization, solvent-free preparation, and easy control.It can be used for large-scale and large-area production and is suitable for current commercial and industrial applications. 23Depending on the power supply frequency, magnetron sputtering methods are classied into direct current (DC) sputtering and radio frequency (RF) sputtering.During DC sputtering, the substrate is connected to the negative electrode as the cathode, and the anode is connected to the sputtering material.When RF sputtering, the substrate is usually connected to the ground, and the sputtering material is connected to the high-frequency power supply. 49The sputtering of perovskite lms consists of four steps, as shown in Fig. 3a.(1) Ions are formed in the plasma and directed towards the perovskite target.(2) Ion-sputtering of the perovskite target occurs.(3) The ejected atoms are transported to the substrate.(4) The atoms condense and form a lm on the substrate.The impact of atoms or ions sputters the surface due to the exchange of momentum between the high-energy material and atoms within the cathode target. 50Compared to thermal evaporation lms, sputtered lms have a higher density, smaller particle size, better adhesion, and exhibit overall properties closer to the characteristics of bulk materials.The choice between DC and RF sputtering usually depends on the requirements of the particular application and the desired lm properties.Fig. 3b shows a sputtering system that can achieve both DC and RF sputtering.
Magnetron sputtering was used to prepare perovskite lms to form a high-quality active layer of high-performance polyvinyl chloride (Fig. 4). 51Perovskite materials can be effectively prepared by mechanical synthesis. 52,53In the straightforward mechanochemical method of producing halide perovskites, individual precursor powders, such as methylammonium iodide (MAI) and PbI 2 , are ground together with a mortar and pestle until the perovskite is formed, which is usually indicated by color changes. 23Finer and more controlled processes involve the use of a ball mill, such as a shaker or planetary ball mill. 54he reactant powder is weighed to the desired stoichiometry and added to the grinding vessel along with grinding balls, commonly made of stainless steel or toughened zirconia.Occasionally, a liquid abrasive (e.g., cyclohexane) is added for wet ball milling (liquid-assisted grinding). 53,56The grinding tank is sealed tightly, inserted into the mill, and the synthesis process begins under the mechanical crushing by the balls. 55he mill pulverizes the reactants, thereby providing reaction energy through shock and friction. 57At longer timescales, the plastic deformation dynamics of the powder particles accelerate and initially dominate. 58The mechanically synthesized perovskite powder is subsequently molded and pressed into a target of a specic shape.For example, Cs 2 AgBiBr 6 powder was initially formed into a cake and then subjected to a pressure treatment at 200 MPa using a hydraulic press. 23Additional annealing treatment further enhanced the crystallinity and grain growth.The perovskite target was installed in a magnetron sputtering instrument and sputtered onto a substrate to prepare the perovskite lm.During sputtering, Ar + ions bombard the target material to form perovskite clusters.Finally, a high-quality perovskite lm was obtained.
1][62][63] For instance, perovskite lms have been deposited directly on mesoporous TiO 2 substrates by sputtering MAPbI 3 from a single target. 23Through post-treatment involving Cl doping and MAI/MA gas treatment, the defect density was reduced, leading to a successful increase in the PCE from 15% to 17.1%. 24Liu et al. rst demonstrated a solvent-free method for preparing perovskite thin lms for high-PCE PSCs via vapor deposition, in which the perovskite precursors were thermally evaporated in a vacuum chamber and deposited on the substrate. 60Furthermore, a laminated chemical vapor deposition technique for mixed-cationic PSCs incorporating self-passivation and gradient absorption layers was demonstrated. 39Magnetron sputtering enables mass production suitable for current commercial and industrial applications, and is commonly used to deposit the HTL and electron transport layer (ETL) of PSCs. 64,65Sputtering has also been proposed for perovskite lm preparation, although device applications remain limited. 21,66Considering their specic properties, the other two most distinctive perovskites are the hybrid halides CH 3 NH 3 PbI 3−x Cl x and HC(NH 2 ) 2 PbI 3 composed of formamide (FA) cations. 67The incorporation of chlorine into CH 3 NH 3 -PbI 3−x Cl x enhances the carrier transfer at the heterojunction, 68 whereas FAPbI 3 -based devices exhibit broader infrared absorption. 69The perovskite materials were converted from powders to lms via magnetron sputtering and post-treatment (MAI and MA gas vapor-assisted treatment). 23Notably, this process is benecial for manufacturing tandem solar cells with a PCE improvement of nearly 60% relative to PSCs without postprocessing.As shown in Fig. 5a, 24 in contrast with the use of the pure MAPbI 3 phase, PbCl 2 in the perovskite lm prepared by magnetron sputtering reacted with MAI during the gas-assisted treatment process, resulting in the successful introduction of Cl atoms to form MAPbI 3−x Cl x .The transformation from a solid perovskite lm (CH 3 NH 3 PbI 3−x Cl x (s)) to a liquid perovskite lm (CH 3 NH 3 PbI 3−x Cl x $xCH 3 NH 2 (l)) occurs during MA gas introduction, resembling the dissolution of stacked solid perovskite nanoparticles into a continuous liquid phase. 24,70The subsequent removal of MA gas transforms the liquid perovskite lm back into a solid form (formula (1)), resulting in a compact and smooth lm with few pinhole defects.This Cl introduction process enabled the PCE of the PSC to be increased to 17.1%. 24 Because magnetron sputtering operates based on the principle of momentum exchange, a wide range of materials can be fabricated, such as various metals and oxide ceramics. 24,71All functional layers of a PSC can be prepared by magnetron sputtering. 23,46,72,73Replacing the organic charge-transport layer with a sputtered inorganic layer both reduces the cost and improves stability.However, subsequent deposition on the perovskite layer can damage the so lattice structure of perovskite materials.To address this issue, a protective layer of PMMA and PCBM was deposited on the top of the perovskite layer by spinning coating to prevent further sputtering charge transport layer from damaging the perovskite layer (Fig. 5b-d). 22he protective layer prevents the perovskite from being damaged by subsequent SnO 2 deposition while maintaining efficient charge transfer, resulting in a PCE increase from 14.62% to 17.43%. 22These ndings demonstrate the considerable potential of magnetron sputtering in the preparation of all functional layers in PSCs.This innovative preparation process opens up new avenues for the industrialization of PSCs.
Applying an excessively high voltage during the sputtering process results in larger sputtering particles, leading to the formation of a rough lm.Conversely, an excessively low voltage slows the sputtering process, causing perovskite decomposition. 74In addition, the thickness of the perovskite lm plays a crucial role in device performance and can be controlled by adjusting the sputtering time. 23It was proposed that the optimal conditions for forming ∼400-500 nm perovskite layers were as follows: an applied voltage of 800 V, pressure of 9.6 Pa, and sputtering time of 5 min, conducted in an atmosphere with less than 30% humidity or in a nitrogen environment. 23To avoid the emergence of pre-liquids and improve the performance of PSCs prepared using solvent-free methods, many researchers have explored alternative processing methods.For example, a solid-state in-plane growth method was presented, which involves applying pressure and heat to grow twodimensional (2D) layers on top of 3D layers, ensuring the consistent performance of the layers across the device. 75This approach successfully avoids the formation of unexpected phases, and allows the thickness of the 2D layer to be adjusted.The controllability of the 2D layer thickness facilitates device optimization to increase the built-in potential at the junction, which resulted in a stable PCE of 24.35% and high stability. 75owever, the overall operational process is intricate, costly to control, and not readily scalable for large-scale production.7][78][79][80] Consequently, more efforts are required to nd a cost-effective, scalable solvent-free method for preparing high-performance PSCs.

Perovskite surface defects and general improvement strategies
In high-quality perovskite lms, surface defects are the main factor affecting the performance of PSCs, especially Pb vacancies, I vacancies, and Pb-I inverses. 81Various approaches have been employed to mitigate these surface defects, such as adding additives to the precursor solution, anti-solvent treatment, and post-treatment.These strategies introduce compounds that form coordination or ionic bonds with the charged defects within the perovskite structure. 24,82These passivating agents neutralize charges at the defect sites and reduce the disruptive effect of electrons on the ionic lattice, thereby affecting the structure of the perovskite layer. 83These agents also signicantly affect lm formation, further altering the volume defect concentration and terminating the perovskite surface.Effective interface management by post-processing is essential for improving both device PCE and stability.5][86] To study the control of Pb-based defects, the effect of amphoteric 2-methylthio-2-imidazoline (MT-Im) cations on the formation of interface defects of a new lowdimensional perovskite (LDP) was reported. 87The defectforming energy of perovskites containing MT-Im was calculated using density functional theory (DFT). 88Compared with the formation energy of neutral defects on the perovskite surface, 89 the effect of MT-Im on the formation of Pb-I antiposition defects in the perovskite was signicantly higher than that of the control.This indicates that MT-Im has a pronounced passivation effect on the Pb-based defects in the 3D perovskite lms.
Fig. 7a shows a schematic of the effects of common surface defects and additives on perovskite lms. 90Major defects at the surface or grain boundaries of perovskite crystals can lead to deep traps, such as incongruous halide ions or Pb 2+ , and Pb clusters, and occasionally some inherent point defects caused by certain growth or processing conditions, such as Pb-I antiposition defects (PbI 3 ). 91The surface of a control perovskite lm was rough with an average grain size of 595 nm, as shown in Fig. 7b. 76Aer treatment, the smooth surface can reduce the probability of local contact between the top and bottom perovskite lms, thus preventing the formation of large void defects.Moreover, the wide grain boundary valley facilitated the elastic deformation of the perovskite lms under applied pressure in the maximum strain range of 5% (the elastic modulus of the perovskite lms was 10-20 GPa). 30Subsequently, the plastic deformation of the perovskite lm was caused by heat transfer from top to bottom, yielding an optimally layered perovskite lm through a hot-pressing process.[78][79][80] Fig. 7  pinhole-free, and at morphology.Notably, the perovskite lms produced by hot pressing sublimation (HPS) treatment had larger single-layer particles. 33The appearance of sufficient PbI 2 units near or at the grain boundaries results in the formation of PbI 2 clusters, which act as barriers that impede further expansion of the grain boundaries, thereby inhibiting perovskite crystal growth. 92Prolonged or high-temperature thermal annealing leads to the loss of chloride ions through the formation of CH 3 NH 3 Cl (MACl), which leaches from the perovskite lattice, and the formation of PbI 2 , which signicantly affects the long-term stability of PSCs.Conversely, excessive MAI results in a strong release of MACl, leading to poor-quality perovskite lms with large pinholes, subsequently reducing the overall cell performance. 93In formula (2), MAI replaces most of the MACl at the grain boundaries, allowing the majority of MACl to escape from the perovskite lm. 33The active MAI vapor and exchange reaction between MAI and MACl activate the grain boundaries, promoting the rapid migration of grain boundaries and grain growth.The optimal orientation and large grain size effectively inhibited volume and/or surface recombination of the perovskite lms. 12,94 The abovementioned methods focus on the treatment of the exposed upper surface of the perovskite because this is easier to modify than the hidden lower surface. 12,76,80However, optimizing the lower perovskite surface is very important.Owing to the growth direction of the perovskite from bottom to top, the periodic structure must be terminated, and the perovskite lattice inevitably dissolves the upper surface of the perovskite lm in the range of tens of nanometers, resulting in many defects and the formation of amorphous phases (Fig. 8a). 95The surface of the underlying ETL is used as the starting point for 3D periodic perovskite lattice epitaxial growth, which can be alleviated. 96Potassium chlorobenzene sulfonate was used as a new multifunctional agent to modify the buried tin oxide (SnO 2 )/perovskite interface of conventional polyvinyl chloride. 97he enhanced carbon-chlorine bonds effectively interacted with the uncoordinated Sn atoms, effectively lling the oxygen vacancies on the SnO 2 surface.The synergistic effect of functional-group-rich organic anions and potassium ions can reduce the defect density, carrier recombination, and hysteresis.A high PCE of 24.27% was achieved for the improved device.A SnO 2 ETL treated with formamidine sulfonic acid (FSA) ions helped rearrange the stacking direction, orientation, and distribution of the residual PbI 2 in the perovskite layer, thereby reducing deleterious side effects of residual PbI 2 . 98FSA functionalization also modied the SnO 2 ETL to suppress deep defects at the perovskite/SnO 2 interface.
In addition to a high defect density, the buried interface also has problems related to residual strain, low crystallinity, excessive ion migration, and harmful voids. 43,99Research on passivating agents has not yet found a comprehensive solution to these problems.The construction of benign buried interfaces remains an ongoing challenge, particularly when passivationfree approaches are used.g-CsPbI 3 solid-solution epitaxial growth without strain was achieved using an a-BaF 2 nanoparticle substrate. 96The prepared g-CsPbI 3 thin lms were uniform and smooth.The lattice match between the highly exposed surface on the a-BaF 2 nanoscale heteroepitaxy growth substrate and the g-CsPbI 3 (110) surface was 99.5% (Fig. 8b-e).A transparent and conductive perovskite (SrSnO 3 ) was demonstrated as an ETL. 43A high degree of lattice matching makes the growth of halide perovskites on the ETL more orderly, avoiding the deterioration of the buried interface.The constructed buried interface exhibited limited defects and strain, better crystallinity, reduced ion migration, and fewer lattice growth inevitably results in poor-quality lower and upper interfaces of the perovskite lms, respectively.By utilizing ETL layers that better match the perovskite lattice and surface treatment of the upper surface of the perovskite, poor initiation and fewer terminations of amorphous phases can be achieved, resulting in more efficient PSCs.

Device performances
Due to the low cost, solution processability, and unprecedented rapid improvement in photovoltaic performance, PSCs are currently the focus of next-generation photovoltaic research. 66,100able 1 summarizes the properties of various functional layer materials constituting PSCs and their respective devices.Functional-layer materials such as ETLs/HTLs exhibit minimal alterations, primarily achieved by perovskite component engineering, surface engineering treatment of functional layers, or improving processing technology to optimize PSC performances.
The solar cells composed of perovskite active layers commonly used in the past ve years are selected, and each solar cell was treated by different methods.By comparing the PCE of each device, it is found that the efficiency of the device prepared by solvent-free method and hot-pressing self-assembly is generally lower than that of the traditional method.Therefore, although the preparation of solar cells by solvent-free method or hotpressed self-assembly can reduce the high cost and solution toxicity caused by traditional methods, the improvement of its PCE needs to be further improved.
Understanding the degradation mechanisms caused by various factors is crucial for developing strategies for improving device performance.Degradation factors are typically classied as internal/inherent factors arising from the internal structural and chemical instability, or external factors stemming from the external environment. 2Inherent degradation factors primarily originate from the material itself and the interfaces between functional layers.The mechanisms of degradation caused by external factors need to be better understood to reduce the inuence of internal factors on degradation.To enhance the performance of PSCs, it is essential to understand the degradation mechanisms induced by external factors, given the interactions between external and internal degradation factors. 108External degradation factors such as the water and oxygen concentrations play a signicant role.Water molecules break hydrogen bonds within the perovskite, forming new hydrogen bonds and hydration compounds, leading to high ion mobility and severe water degradation. 1Ions in perovskite can react with oxygen to form charge barriers and electron traps, while oxygen can create Pb-O bonds on the surface of perovskite lms, resulting in severe oxygen degradation. 109Encapsulation partially or completely eliminates degradation caused by water and oxygen.However, external degradation factors such as light and heat, which are challenging to isolate, remain persistent threats to device stability.Understanding and addressing these factors are crucial for enhancing the performance of PSC devices.Overall, internal factors relate to the intrinsic properties of the material and structure, whereas external factors are related to the conditions under which a solar cell is used during its practical application.Optimizing the devices to minimize the effects of the degradation factors can improve the performance and stability of PSCs.
Light exposure can induce ion migration, trap-state formation, phase separation, and photocatalytic degradation, significantly affecting the practical applications of PSCs. 110The photoinduced self-healing process involves two main stages: demixing in stage I and remixing in stage II.Fig. 9a shows the photoinduced self-healing process through I − /Br − ion displacement under continuous illumination. 111Additionally, Fig. 9b shows the reversibility of the photoinduced halide segregation, that is, the photoinduced phase segregation and subsequent recovery under dark conditions. 112Compositional changes that occur naturally before light exposure produce Irich regions with reduced band gaps.Upon irradiation, electron-hole pairs rapidly separate, with carriers moving to lowgap I-rich regions before recombination.In these regions, a substantial number of carriers interact with the high-valence perovskite structure, causing lattice deformation through electron-phonon coupling (Fig. 9c). 90This strain was sufficient to increase the enthalpy of mixing, resulting in a second minimum in the free energy and Br content plot, resulting in the perovskite forming an I/Br-rich phase (Fig. 9d). 90Continual light exposure causes most of the light-excited charges to migrate toward the I-rich, low-gap regions on the lm, where they are extracted and subsequently recombined.Owing to the smaller gap, these carriers produced less voltage than those from the stoichiometric mixed-halide region.However, when the light is removed, the free energy diagram of the perovskite returns to its pre-illumination state, reestablishing the single-phase driving force. 113Therefore, phase segregation is typically reversible displacement under continuous illumination. 111Additionally, Fig. 9b shows the reversibility of the photoinduced halide segregation, that is, the photoinduced phase segregation and subsequent recovery under dark conditions. 112Compositional changes that occur naturally before light exposure produce Irich regions with reduced band gaps.Upon irradiation, electron-hole pairs rapidly separate, with carriers moving to lowgap I-rich regions before recombination.In these regions, a substantial number of carriers interact with the high-valence perovskite structure, causing lattice deformation through electron-phonon coupling (Fig. 9c). 90This strain was sufficient to increase the enthalpy of mixing, resulting in a second minimum in the free energy and Br content plot, resulting in the perovskite forming an I/Br-rich phase (Fig. 9d). 90Continual light exposure causes most of the light-excited charges to migrate toward the I-rich, low-gap regions on the lm, where they are extracted and subsequently recombined.Owing to the smaller gap, these carriers produced less voltage than those from the stoichiometric mixed-halide region.However, when the light is removed, the free energy diagram of the perovskite returns to its pre-illumination state, reestablishing the single-phase driving force. 113Therefore, phase segregation is typically reversible.
In addition, the migration of atoms/ions from organometalide perovskites into the HTL induces degradation, affecting both the PCE and stability of the PSCs. 114Oxygen plays a key role in the photoinduced degradation of PSCs, in which iodine diffuses from the perovskite to the HTL under the inuence of O 2 and light.Photoexcited holes combine with iodine ions, forming neutral iodine with high activity that may diffuse into the HTL, where the iodine activity is signicantly lower. 115In addition, experimental results have shown that O 2 provides enhanced iodine activity and generates iodine vacancies in the perovskite, thereby enhancing the diffusion of iodine outside the perovskite (Fig. 10a). 116,117Iodide migration involves charge transport from the perovskite to the HTL.Therefore, to solve the problem of photoinduced degradation in an oxygenated atmosphere, it is necessary to inhibit the diffusion of iodine or isolate the device from oxygen.A solid buffer layer of PbS deposited on the surface of perovskite effectively increases device stability by preventing perovskite degradation. 80The PbS buffer layer prevented direct contact between the perovskite and water and inhibited ion migration in the buffer layer, resulting in a PSC with signicantly improved long-term stability under high humidity, high temperature, and continual illumination conditions. 80,118urthermore, the PbS buffer layer enhanced the extraction of holes from the perovskite, thereby improving the power conversion efficiency (Fig. 10b). 80Similarly, a layer of np-Al 2 O 3 was deposited between the perovskite and HTL as a diffusion barrier, resulting in a device with good stability against oxygen and light exposure. 117The PSC devices were encapsulated by sealing the surface of the top layer of the device with adhesive sheets, thereby removing the air trapped during lamination.Shelf tests were performed at 85 °C and 85% relative humidity (RH) to assess the package efficiency (Fig. 10c).Aer 1000 h, the PCE of the device remained at 96% of its initial value (20.0-20.9%).Long-term stability tests under actual operating conditions revealed a PCE of 20.6% (96% retention of its initial value; Fig. 10d), highlighting the robustness of the device packaging.
Heat is another inevitable external factor that introduces phase transitions and hinders separation, decomposition, ion diffusion, and charge transport. 119The operating temperature of solar cells can rise to 85 °C, while the phase transition of the most commonly used perovskite material (MAPbI 3 ) usually occurs at 60 °C. 119The liquid crystalline nature of perovskites facilitates the movement of ions. 1202][123] The difference in spectral characteristics between bromide and iodide perovskite lms makes it possible to track the movement of halide ions.5][126][127][128][129] While the migration rate of halide ions is slow at room temperature, it increases signicantly at elevated temperatures, leading to an accelerated rate of dark reduction. 4The mixing entropy explains the thermally activated mixing of halide ions to produce mixed-halide perovskites. 124,130,131hi et al. introduced a method for graphing the stability as a function of PCE, by employing a quantitative analysis to provide insights for material selection, development, and structural design to achieve a balance between PCE and stability (Fig. 11a). 108There are two fundamental strategies for enhancing the performance of PSCs: component and interfacial engineering.Composite material engineering is realized through the material development of each main layer and metal electrode. 132Although the formation of a uniform solid solution is not always guaranteed, certain combinations of A-site cations and B-site halides in perovskites are superior to their singlecation/halide counterparts in terms of both PCE and stability. 2nterfacial engineering further improves device performance by passivating the primary layer to reduce defects and/or inserting a protective layer around the fragile perovskite absorption layer and the ETL to mitigate degradation factors. 133Fig. 11b-e illustrate the various improvement strategies.However, achieving both high PCE and stability is a major challenge.Specically, it is difficult to quantify stability while enhancing the PCE.This stems primarily from the absence of standardized aging measurement conditions and criteria.Perovskite absorbers, which are the main source of device degradation owing to their inherent instability, signicantly inuence the device PCE and stability. 1081.PCE MAPbI 3 usually undergoes a phase transition from the tetragonal to cubic phase at temperatures of 54-57 °C.135 Organic MA cation volatilization occurs at higher temperatures because of the weak bonding and low formation energy.The thermal degradation of perovskite materials can be explained by the Goldschmidt tolerance factor, which is an empirical indicator reecting the stability of perovskite crystals based on the ionic radius within the crystal lattice.136 Perovskite materials exhibit good stability when the tolerance factor is in the range of 0.8-1.0.Deviations from this range lead to severe thermal degradation due to lattice distortions.137 Many efforts have been made to improve the coverage and quality of perovskite lms, such as the optimization of the precursor solution, deposition conditions, and post-treatment.For instance, additives like PbCl 2 are used to regulate the crystallization kinetics of perovskite lms, resulting in better lm coverage, reduced defects, and increased carrier diffusion length.[138][139][140][141][142][143] The combination of large FA and small Cs is benecial for the formation of the preferred black perovskite phase, removal of volatile substances, and improvement of thermal stability. 108Therefore, substituting MA with Cs and FA is an efficient approach for fabricating thermally stable PSCs.By adjusting the composition of the A and X sites, the thermal stability of low-or high-PCE PSCs can be signicantly improved.144 Owing to the same electron conguration, Sn is a good substitute for Pb; however, Sn 2+ is easily oxidized to Sn 4+ , which greatly reduces the stability of the perovskite.134 The incorporation of Pb and Sn helps to reduce the oxidation of Sn 2+ , promote the transformation of PbI 2 into a perovskite phase, diminish grain boundaries, enhance crystal quality, increase the open-circuit voltage (V oc ), and improve the overall PCE and stability.For example, a MAPb 0.9 Sn 0.1 I 3 PSC device, in which Sn partially replaced Pb, maintained 90% of its original PCE of 18.3% aer 500 h of illumination.77 Moreover, the introduction of Br into Sn-based PSCs further improves their stability owing to the reduction in Sn vacancies.
Although the PCE of PSCs has improved rapidly, long-term stability problems persist under different conditions.2D PSCs have the advantage of high stability based on interfacial cations alternating between amino and halogen ions; however, 2D PSCs exhibit low PCEs compared to 3D devices. 145This discrepancy arises from the limitations imposed by the 2D structure on the efficient transmission of principal charges.This issue was addressed by incorporating a linear short chain of tetraethylene pentamine (TEPA) into a perovskite structure to modify its symmetry. 139Devices based on TEPA-MAPbI 3−x Cl x had a higher PCE compared to the original PSC based on MAPbI 3−x Cl x (Fig. 12a). 139Furthermore, a heterocycloammonium salt cation (2-methylthio-2-imidazoline; MT-Im) LDP passivation layer was added to a perovskite lm. 87The growth of the mixed-phase LDP introduced a strong interaction with under-coordinated Pb 2+ on the surface of the perovskite lm.Although the addition of MT-Im did not alter the crystal structure of the perovskite (Fig. 12b), 87 two new diffraction peaks appeared, indicating the formation of mixed-phase layers on the bulk perovskite surface. 47,146These peaks corresponded to the (MT-Im) 2 PbI 4 and (MT-Im)PbI 3 mixed-phase layers (Fig. 12c).The PCE of the improved device increased by 24.07%(Fig. 12d).As shown in Fig. 12e, as electron donors, C]N and -S-CH 3 with electron lone pairs in MT-Im exhibit strong Lewis acid-base interactions with unpaired Pb 2+ , forming Pb-N and Pb-S coordination bonds. 147Nitrogen also interacts with -NH 3 + in perovskites to form hydrogen bonds.These synergistic effects result in a robust passivation effect. 130,131This prevents fewer nonradiative composite centers and enhances the connection between the surface LDP and the massive perovskite, facilitating the separation and transfer of internal electrons and holes.

Stability
The PCEs of PSCs have been successfully improved by additive engineering and surface passivation.][150][151] The stability limitations of PSCs are classied into external and internal factors.External environmental factors can be prevented by using external packaging.Intrinsic factors such as photoinduced decomposition, ion migration, and thermal degradation 152 must be addressed to improve the quality of perovskites.The PCE and stability of PSCs are inuenced by the presence of defects, such as the Pb-I inverse and unpaired metallic lead (Pb 0 ) at the interface. 874][155][156] For high-performance PSCs, Pb 0 caused by the thermal annealing of perovskite lms or degradation of the interface between the perovskite and ETL should be avoided. 38,157t was found that Pb 0 defects are a byproduct of the decomposition of residual PbI 2 in the perovskite under light or X-ray irradiation (Fig. 13a). 17In contrast, perovskites without excess lead halides demonstrated a reduced propensity to form Pb 0 impurities, exhibiting better tolerance to light and X-ray exposure.The presence of Pb 0 hindered perovskite crystallization, increased deep-layer defect levels, reduced trap activity, enhanced nonradiative recombination, and accelerated perovskite degradation. 38,158Therefore, the PCE and stability of PSCs obtained from photoaged lead-iodide lms containing Pb 0 impurities were signicantly reduced.Furthermore, a europium ion pair (Eu 3+ -Eu 2+ ) was used as a redox shuttle to selectively oxidize Pb 0 and reduce I 0 defects simultaneously during cyclic phase transitions. 159The synthesized device achieved a high PCE while maintaining long-term stability (Fig. 13b).Eu 3+ can easily be reduced to Eu 2+ with a stable half-full f7 electron conguration, forming naturally bound ion pairs. 12The redox shuttle facilitated the transfer of electrons from Pb 0 to the I 0 defect through a cyclic process, where Eu 3+ oxidizes Pb 0 to Pb 2+ , and the resulting Eu 2+ simultaneously reduced I 0 to I − (Fig. 13c).The reaction between Pb 0 and I 0 is thermodynamically favorable, with a standard molar Gibbs formation energy of 173.6 kJ mol −1 for PbI 2 (s), 159 which provides the driving force for the elimination of these two defects.The proposed redox shuttle eliminated the corresponding defects based on the following chemical reactions: 159 2Eu 3+ + Pb 0 / 2Eu 2+ + Pb 2+ (3) The stability of PSCs is essential for meeting the requirements of industrial and commercial applications.However, their poor stability has become a major bottleneck restricting the comprehensive performance of PSCs and has thus attracted much research attention. 160Achieving a highly stable perovskite requires that the tolerance factor is kept within a range of 0.8-1 and preferably maintaining a cubic phase with a tolerance factor of 0.9-1.Tolerance factors can be modulated by changing or mixing ions of different sizes, which offers a promising avenue for enhancing stability. 2The introduction of mixed cations promotes the growth of crystals with preferred orientations and the formation of smooth perovskite lms.This reduces the number of trap states, accelerates the extraction and transport of electrons, reduces charge recombination, and enhances thermal stability. 108Mixing halides is benecial for reducing oxidation under light illumination, increasing the charge-transport rate, adjusting the bandgap, and consequently improving stability.The substitution of I − with Cl − ions at the X site promotes carrier transport and device stability.Cl − at the X site facilitates the crystallization of MAPbI 3 , increases the diffusion length of carriers, accelerates charge transfer, and enhances carrier collection, thus improving efficiency and stability. 108PSCs are susceptible to inherent structural instabilities associated with the presence of inorganic halide anions and organic cation vacancies, resulting in the deterioration or even premature failure of devices.The partial substitution of I − by BH 4− reduces the vacancy density, inhibits recombination, and forms a smooth, dense, and high-quality perovskite lm, which enhances the PCE and stability. 78Br and I − have similar ionic radii, and partially replacing I − with Br results in a cubic rather than a tetragonal structure, reducing octahedral tilt and lattice distortion.Combining Br and I compresses the lattice, increases the binding strength of MA-Pb, increases the grain size, and improves the PCE and thermal stability. 161However, excessive Br at the X site can cause halide segregation, resulting in dephasing, the formation of I-rich inclusions that act as recombination centers, and poor PSC stability.Optimizing the Br concentration is crucial for obtaining stable PSCs with high PCE.Although ion substitution at the A and/or X sites plays a dominant role in improving performance, the substitution of Pb 2+ at the B site contributes to enhanced photostability and thermal stability.This was attributed to high light absorption, long carrier lifetime, low charge-transport resistance, high carrier-recombination resistance, and low trap density. 78ompared to 3D perovskite devices, devices using lowdimensional perovskites, in which some or all cations are replaced by large organic ligands, show greater stability against heat, light, and moisture during long-term operation. 144,145For example, the development of damp-heat-stable PSCs involves tailoring the dimensional fragments of a 2D perovskite layer.This layer, formed by oleoamine-iodized molecules at room temperature, effectively passivated the perovskite surface at the electron-selective contact. 154The resulting inverted PSCs exhibited a PCE of 24.3% under wet-heat test conditions and maintained 95% of their initial value aer 1000 h (Fig. 14a), thus meeting one of the key industrial stability criteria for photovoltaic modules. 16However, large ligands hinder charge transfer and reduce efficiency (Fig. 14b). 16It was found that aer 500 h of continuous operation, the initial PCE of a Br-rich device remained above 80% (Fig. 14c). 162This device showed the best operational stability among PSCs prepared by sequential deposition methods and was even comparable to PSCs prepared using a one-step anti-solvent droplet method.This emphasizes the signicance of the Br content in enhancing the operational stability of PSCs. 163The high bromine content stabilizes the perovskite phase of FAPbI 3 , making it thermodynamically favorable and achieving superior thermal stability. 164In addition, because iodide anions exhibit low ion migration activation energies, particularly under light, their easy migration during operational stability tests can degrade PSC device performance.Therefore, substituting bromine with iodine can enhance the operational stability of PSC devices.Alternatives such as shortchain cations 165 and conjugated cations 166 can potentially increase the PCE without sacricing stability (Fig. 14d).By exploiting the hydrophobicity of large cations, the stability of perovskites can be effectively improved by adjusting their dimensions. 167Protecting the perovskite interfaces and grain boundaries is another way to slow degradation.

Thermocompression self-assembly PSCs and properties improvement strategies
Currently, the main methods for improving the quality of perovskite lms are based on post-fabrication hot pressing or pressurization during PSC packaging.However, these methods introduce additional operational steps and require consideration of solvent compatibility and thermal budget constraints. 143onsequently, some researchers have proposed dividing PSCs into two separate devices for hot-press assembly as a potential solution to these challenges (Fig. 15). 28,30,33,76,101,103,168,169Notably, this approach resulted in three different interface types: HTL/ perovskite, ETL/perovskite, and perovskite/perovskite.Jung et al. studied three interface forms formed by hot pressing. 28hey observed that with the transformation of the perovskite surface into a block, the PSCs exhibited a buried interface solely between the perovskite layer and two functional transport layers.The hot-pressing process facilitated the development of larger perovskite grains as well as smoother and denser interfaces.This resulted in a reduction in the defect and trap densities and repressed ion migration and phase segregation under light  exposure.Moreover, the hot-pressed perovskite layers demonstrated enhanced water resistance.The conventional layer-bylayer solution treatment of lead-halide perovskite devices imposes limitations on their structures.The layer beneath the perovskite must withstand the strong organic solvent used during perovskite formation, whereas the layer above operates within a limited thermal budget and must be treated with a nonpolar solvent to prevent perovskite degradation. 13Because the phase segregation of mixed-halide perovskites involves the migration of halide ions.The crystal defects and strain lattices at the grain boundaries allow active ions to migrate from the grain boundaries, thereby accelerating halide segregation. 127ven in single-halide perovskite systems such as MAPbI 3 , ion migration has been identied as a primary driver of degradation. 126,170,171Both single-halide and mixed-halide perovskites can benet from an increase in the activation energy of ion migration, which effectively reduces the degradation rate and extend the operational lifetime of the device.As the pressure increased, the nal mixing ratio of the separated phase approached that of the mixed phase, thereby altering the thermodynamic pattern of phase segregation. 172In addition, it was found that phase segregation was much slower at high pressures for all MAPb(Br x I 1−x ) 3 mixing ratios (x = 0.25, 0.5, and 0.7). 170The enhanced activation energy of halide migration under a compressed unit-cell volume indicates an increased barrier to halide diffusion into vacancies under pressure. 114This suggests that a reduction in the unit-cell volume achieved through component engineering or physical pressure can effectively delay halide migration by increasing the activation barrier of the migration process.Lamination not only reduces the band gap of the perovskite, but also preserves or sharpens the characteristics of the absorption band edge, corresponding to changes in the structure and associated defects of the conduction and/or valence band edges. 173Additionally, reducing the grain boundary open space and limiting the content of mobile ions at the grain boundary can inhibit the migration of mobile grain-boundary defects, thereby inhibiting halide segregation. 103urrently, the main methods for perovskite lm treatment involve hot pressing of either the perovskite lms themselves or the entire PSC.In the former approach, a thin perovskite lm is deposited onto a suitable substrate and subjected to hot pressing at high temperature (typically 100-200 °C) and pressure (usually 10-50 MPa). 76,174,175This helps improve the perovskite crystal structure and reduce defects.For instance, a metal halide perovskite (MHP) lm was deposited on clean bare glass and hot-pressed at various temperatures and a pressure of 80 MPa (glass cannot withstand 100 MPa). 103y limiting the growth of grains in the plane direction, openstructure grain boundaries were transformed into dense GBs, thereby improving structural homogeneity.This inhibits defectmediated ion migration at the grain boundaries, resulting in MHP solar cells with PCEs exceeding 11%. 103Full-device treatment involves heating the prepared PSC in a hot-press machine, thereby enhancing the interfacial contact between the perovskite lm and the HTL and ETL.For example, a stack was placed in a hot press and annealed in a nitrogen-lled glove box at 150 °C and 2 MPa for 5 min, resulting in a PCE of 10.6%. 101It was found that the self-assembly of PSCs in two stacks increases the PCE while reducing the number of preparation steps. 28This innovative technique involves laminating two separately treated half-stacks, enabling the use of unique device architectures and greater exibility in selecting the ETL and HTL materials. 169As mentioned earlier, the application of hot pressing during lamination can improve the crystal quality of perovskites, thereby reducing the defect density, leakage current, and iodine migration in the perovskite. 28The performance of PSCs prepared by hot pressing is highly dependent on the applied pressure and temperature, as summarized in Table 2. Additionally, factors such as doping of the perovskite or surface passivation signicantly affect the performance.Therefore, a detailed analysis of the various inuencing factors and an understanding of their mechanisms are crucial for improving PSC performance.The enhancement mechanisms employed in the solution preparation of PSCs should also apply to solventfree processes.

Composition-based enhancement
In MHPs with the ABX 3 structure, the metal-halide cage of the BX 6 octahedron forms a lattice around cation A with relatively weak metal-halide bonds.This so lattice is susceptible to the structural disturbances associated with point defects. 1779][180][181] As the stoichiometric ratio increases, the grain size decreases (Fig. 16a). 175A sub-stoichiometric layer contained larger grains with smaller grain boundary areas, whereas an over-stoichiometric layer contained smaller grains with larger grain boundary areas.The ow ion density and total ion defect density decreased with increasing grain size.This trend suggests that the observed defects were primarily located within the bulk, although it is crucial to note that the grain size variation was achieved through a fractional deviation in the precursor stoichiometry. 182Therefore, the relative contributions of the grain volume and grain boundary cannot explain the magnitude of the change in the ion defect density.In contrast, the change in defect density is a direct result of the inuence of chemometrics on the defects. 114The formation enthalpy exhibited changes corresponding to the grain size, indicating that samples with larger grains and smaller grain boundary areas require more energy to form defects, and vice versa.A similar trend was observed for the enthalpy of migration, signifying that the energy barrier for ions to jump between lattice sites decreases with decreasing grain size. 114,183,184HPs commonly contain organic cations such as MA + and FA + and classical inorganic cations such as Cs + , resulting in two categories: Cs-based fully inorganic MHPs and organic cationbased MHPs.18 For instance, RF sputtering was used to grow large-area CsPbBr 3 lms with uniform structures and compositions (Fig. 16b and c).21 Temperature-dependent resistivity measurements revealed typical heat-activated electrical behavior and a band gap of 2.24 eV was obtained, providing insights into the potential large-scale commercial production of PSCs.21 Trihalide alloys (chlorine, bromine, and iodine) were used to adjust the bandgap and stabilize the semiconductor under illumination (Fig. 16d and e).185 The substitution of iodine with bromine enhances chlorine solubility by reducing the lattice parameter, resulting in the doubling of the photocarrier lifetime and charge-carrier mobility.161 The photoinduced phase separation in the lm was inhibited even at 1-sun condition, and the degradation rate of the translucent top battery was less than 4% aer 1000 h of operation at the MPP and 60 °C. Both mixed organicinorganic and metallic perovskites are variants of the same basic structure.186 The perovskite structure can be regulated by changing the elements and structural parameters at the A, B, and X sites to form more variants and derivatives.This inherent exibility makes perovskites highly interesting and valuable for scientic and engineering applications.

Pressure-induced enhancement
Pressure is a unique variable that can be used to control the electronic structure and performance of organic-inorganic PSCs. 187The application of pressure induces dense packing and  reduces the atomic distances, potentially leading to alterations in the electron orbitals and bonding patterns.Therefore, the application of pressure can alter the structural, optical, magnetic, and electronic properties of both organic and inorganic solids.Furthermore, an appropriate pressure can strengthen the contact between the layers within the solar cell structure, offering a means of impeding crack propagation along the interfaces. 188Consequently, understanding the effect of pressure on the perovskite material layer enables the improvement of material properties through compression.Unlike temperature, pressure did not appear to exert a signicant inuence on the grain size.These data can be described by the Turnbull model of solid grain growth, 168 which averages the grain size data collected from lms under different pressures at each given processing temperature: where r 0 is the average grain radius before coarsening (here, the average grain size before hot pressing), r t is the average grain size at time t (60 s), T is the process temperature, and R is the universal gas constant.The tting parameters are the prereference constant k 0 and molar activation energy Q of grainboundary movement, which is related to the solid-state diffusion of the relevant substance. 189Under high-pressure conditions, the photoelectric characteristics remained robust even at elevated temperatures, accompanied by an increase in the series resistance.By controlling the growth conditions and regulating the concentration of shallow defects in the donor or recipient material, the inherent conductivity of MAPbI 3 can be modied from p-type to n-type. 82For example, recent studies have shown that exposure to excess I 2 vapor pressure can produce intrinsic p-type conduction in MAPbI 3 . 190,191he application of pressure signicantly enhanced the PCE of the PSCs compared to those without pressure (Fig. 17a-c). 31SC stacks were also thermally pressed on one side, and it was found that continuous pressing at higher pressures degraded device performance (Fig. 17d-f). 30Extrusion-induced increases in compound resistance were observed, which were attributed to reduced charge-carrier capture at interfaces and improved ETL/perovskite and/or perovskite/HTL interfaces, leading to a reduction in the cell hysteresis index aer compression. 192The primary factor contributing to the enhanced PCE was the increased ll factor, which mainly stems from a decrease in the series resistance.Specically, 400 mbar pressure was effective for encapsulating PSCs. 193In contrast, the excessive pressure of 1000 mbar commonly used for commercial silicon solar modules can lead to the "sinking" of particles at the interface, 187 potentially damaging the layers and reducing overall system efficiency.Pressure drives structural changes in perovskites, and the redenition of the boundary conditions of the electron wave function inevitably affects the optical properties. 194For instance, in the inorganic trihalide perovskite CsPbBr 3 , the bivalent Pb cation is octahedrally coordinated by the halide Br anion (Fig. 17g). 187Below 2 GPa of applied pressure, the bond lengths and angles were shortened under high pressure, resulting in a condensed lead bromide octahedron.Aer further compression, the compound eventually evolved into an indirect bandgap structure owing to considerable distortion of the more compact octahedral skeleton to accommodate the Jahn-Teller effect.This highlights the close relationship between the band conformation of the perovskite and the crystal structure.This is consistent with the previous nding that excessive pressure can reduce the performance of PSCs.
The grain boundaries of the samples treated with post-heat pressing (PHP) showed lower depths and narrower widths. 111lthough the exact geometry of grain boundaries measured by atomic force microscopy (AFM) may be inuenced by tip surface convolution effects, conducting comparative studies with statistical averages from the same tip mitigates this concern. 195he ndings of these studies further conrmed that PHP treatment induced the in-plane growth of the lm, restructured the grain boundaries from a porous to dense structure, and reduced structural inhomogeneity.Similarly, the average domain size of a target perovskite lm aer HPS was 3.22 mm, while that of the control perovskite lm was only 283 nm. 33arger grains form wider grain boundaries, which provide larger interfacial areas that better separate electrons and holes, thereby increasing the PCE of photogenerated charge collection. 53,186In traditional spin-coating methods, perovskite lms form defective, porous grain boundaries with original distorted structures. 103The PHP process involves selective grain growth in the plane under high pressure, which transforms these boundaries into dense and oriented structures.The application of moderate pressure can signicantly increase the PCE of PSCs, 185 which is attributed to the closure of voids and a corresponding increase in the interfacial surface contact length with increasing pressure (Fig. 18a and b). 31 Applying moderate pressure to PSCs can improve the interfacial contact between the sandwich particle layers.However, at higher pressures, the absorption of trapped impurities/particles can damage the surrounding layer, thereby reducing the light-conversion efficiency of the solar cell (Fig. 18c).Therefore, selecting the appropriate pressure for hot-pressing PSCs is crucial.
It was showed before the surface morphology of a perovskite under different pressures (Fig. 19a-c). 75Under 20 MPa, the 2D crystals remained in the process of formation, whereas under 60 MPa, the 2D crystals were nearly attened, indicating that excessive pressure can reduce the crystallinity of the perovskite surface.In addition, the high compressibility of iodide resulted in a lower ion-size mismatch with decreasing pressure, reducing the microscopic strain in the mixed system (Fig. 19d). 172In the range of 0-7 MPa, the ( 110) and ( 220) XRD peaks increased with increasing pressure. 31The initial pressure increase induced crystallization, leading to bond length shortening and stress-induced phase transitions, which increased the percentage of (110)-and ( 220)-oriented perovskite crystal phases.However, with a further increase in the pressure (>7 MPa), the ( 110) and ( 220) peak intensities decreased (Fig. 19e) owing to the potential stress-induced amorphous phases caused by cracking and damage. 196The local amorphous phases reduced the overall crystallinity (Fig. 19f-h).Crystal defects at the grain boundaries and strain lattices allowed active ions to migrate from the grain boundaries, thus accelerating halide segregation (Fig. 19i).The reduction in voids and mobile ions at the grain boundaries can limit the formation of mobile defects at grain boundaries, thus reducing halide segregation (Fig. 19j). 103The rate of phase segregation is largely dependent on the pressure applied during PHP, suggesting that strain plays a signicant role in ion migration.Under ambient pressures, a similar reduction in phase segregation can be achieved by inducing strain by regulating the strain in the perovskite lm through a charge-transport layer or by compositional engineering by partially replacing MA + with a smaller cation. 1768][199] Muscarella et al. proposed that light causes thermal expansion strain by weakening Pb-X bonds, which reduces the energy barrier of halide migration. 170Under high pressure, the compressive strain cancels out the photoinduced strain and increases the activation energy of halide migration.Under ambient pressure, I ions move mainly to the illuminated region (dashed circle; Fig. 20) to increase the volume of the rapidly forming I-rich islands.Under high pressure, owing to the high activation energy, halide ions move slowly, resulting in slower phase segregation.
Perovskite layers processed under applied pressure exhibited superior absorbance capacity and were characterized as continuous, uniform, and dense structures (Fig. 21a). 200This is consistent with the observation that the so pressing of perovskite lms removed pinholes and rearranged the structure to obtain uniform and dense perovskite layers (Fig. 21b-e). 42urthermore, cold-rolling and compression increased the contact area between the perovskite and the TiO 2 layer. 200Aer treatment, the perovskite layer changed from a columnar microstructure containing a large amount of uncoated TiO 2 to a continuous and mostly pinhole-free structure and the PCE of the cell increased from 8.16% to 13.24%.This remarkable 62%  increase in cell performance was a result of enhanced charge extraction (Fig. 21f).This emphasizes the signicance of increasing the contact surface area between the layers. 201herefore, in addition to the various hot-pressing methods discussed earlier, the novel cold-rolling pressing technique presented here is a promising avenue for improving the performance of future PSCs.

Temperature-driven enhancement
Perovskites exhibit rapid degradation at elevated temperatures, which is primarily attributed to structural instability induced by electromigration, ion migration, and interfacial interactions. 202otably, as the temperature increased, iodine began to diffuse signicantly below 150 °C, and high temperatures around 175  °C induced lead migration, leading to perovskite degradation and the formation of PbI 2 . 202Ion migration leads to poor longterm stability owing to signicant structural changes such as lattice distortion and phase decomposition. 203,204Additionally, the different distributions of ions in PSCs create different electric eld distributions within the semiconductor, resulting in different device performances.6][207] Moreover, temperature-induced decomposition at approximately 100 °C and phase transition at approximately 57 °C act as catalysts for additional degradation processes. 208The lamination process should encapsulate the product formed by thermal decomposition between the two glass substrates, balancing eqn ( 6) and preventing it from continuing.A direct correlation exists between the hot-pressing temperature and the nal grain size.The grain growth is moderated by ion diffusion. 168Aer annealing, all perovskite lms had large grain sizes but maintained a uniform, pinhole-free, and at morphology.However, lms treated with HPS displayed larger single-layer particles, indicating that halide segregation was inhibited.
In a previous study, a control sample exhibited an average grain size of 501 nm with moderate surface roughness. 103ollowing PHP treatment at 100 °C and 125 °C, the samples exhibited similar average grain sizes to that of the control, yet the surface was attened under elevated pressure.Notably, at PHP treatment temperatures above 150 °C (the critical temperature for grain growth) (Fig. 22a and b), a signicant increase in average grain size was observed. 33Although grain growth is typically isotropic, the PHP treatment hinders out-ofplane growth because of the high-pressure environment, which restricts grain expansion in the in-plane direction. 111,209nnealing without external pressure does not induce alterations in the internal perovskite structure, and halide segregation can only be caused by internal strain in PHP treatment with sufficient heat treatment at high pressure. 185Similar ndings were reported for a lm comprised of small crystal particles with a columnar structure (Fig. 22c). 21During the sputtering of CsPbBr 3 lms, substrate temperatures of 50-200 °C resulted in the complete coverage on the substrate with a pinhole-free lm (Fig. 22d-i). 103Lower temperatures yielded smaller, disordered crystal particles lling the grain boundaries, whereas increasing the substrate temperature gradually increased the particle size.At growth temperatures above 250 °C, the lm surface became rough with prominent grain boundaries and holes. 210Therefore, the substrate temperature has a clear effect on the quality of RF magnetron-sputtered lms.Rapid crystal growth and insufficient particle diffusion at high temperatures were the main reasons for the growth of uneven lms.According to classical nucleation theory, the nucleation and growth of crystals can be explained by differences in the Gibbs free energy due to changes in the volume and surface area of newly formed crystals.To analyze perovskite recrystallization during lamination, AFM images of delaminated PSCs previously processed through lamination were analyzed. 169The layer roughness decreased with increasing lamination temperature.][213][214] At this temperature, the perovskite recrystallized into an exceptionally smooth layer with a root-mean-square roughness of ∼3.1 nm (Fig. 23a). 169A subsequent increase in the lamination temperature further reduced the RMS roughness but did not yield a higher PCE.The crystal structure of the tricationic perovskite remained unchanged under the combined effects of high pressure and temperature.The mixing (or homogenization) process accelerates with increasing temperature, indicating that a thermally activated mechanism governs the mixing/exchange of halide ions.Elmelund et al. summarized the observed temperature-dependent excitation intensity thresholds and indicated that the excitation intensity values for inducing (inhibiting) photoinduced halide segregation at a given temperature were higher (lower) (Fig. 23b). 112The existence of an excitation intensity threshold for phase segregation refutes the polaron strain model. 131Mixing entropy explains the thermally activated mixing of halide ions to produce mixedhalide perovskites. 124,215When the mixed halide perovskite phase is separated, the I-rich domains act as the recombination sites for photogenerated carriers, which limits the performance of halide PSCs. 216,2179][220][221][222] Notably, all-inorganic perovskites require higher temperatures than hybrid organic-inorganic perovskites to stabilize the black cubic perovskite phase (Fig. 23c).In particular, CsPbI 3 requires an annealing temperature of 180 to 330 °C. 218,223Inorganic perovskite lms processed at high temperatures are subjected to greater tensile strain.When the perovskite lm is applied to a layer with a low a (coefficient of thermal expansion), the contact established between the layers during high-temperature annealing restricts perovskite shrinkage upon cooling to room temperature, thereby introducing tensile strain along the in-plane direction (Fig. 23d).Conversely, the use of layers with high a values results in higher shrinkage of the perovskite lm, resulting in compressive strain.Thus, the regulation of tensile or compressive strain in perovskite lms can be achieved by selecting adjacent device layers with lower or higher a compared to perovskite. 176Light-induced halide segregation is reversible owing to thermal activation, allowing the separated region to return to its original uniform composition and the lm to fully recover in dark conditions. 112Fig. 23e shows enthalpy driving the separation process, whereas the entropy drives the remixing process. 172Defects arising from halide-ion vacancies seem to contribute to the separation of halide ions.Hole trapping by iodide ions also induces halide ion migration, requiring that the thermodynamic activation barrier is overcome to prevent the halide ions from recombining. 112Formula (7) describes the migration of halide ions in the opposite direction. 112/2)MAPbBr 3 + (n/2)MAPbI 3 / nMAPbBr 1.5 I 1.5 (7)   This illustrates the thermal-activation-induced exchange of Br and I in mixed lms of MAPbBr 3 and MAPbI 3 .123 Similarly, a pre-separated mixed halide ion membrane required 14 h to fully recover at room temperature, indicating the slow migration of halide ions.112 Nevertheless, as the temperature increases, the rate of dark reduction (mixing of halide ions in the original mixed halide composition) signicantly increases.
For a given plane, a narrower crystal plane spacing implies a more tightly packed atomic arrangement.In addition, the elevated intensity of the PbI 2 (001) peak with increasing temperature (Fig. 24a) indicates an increase in the crystallinity of PbI 2 . 107According to Scherrer's equation, 107 the full width at half maximum (FWHM) of the peak is inversely proportional to the crystal size.A decrease in the FWHM indicated an increase in the grain size of PbI 2 from 65.84 nm to 88.78 nm. 107urthermore, the ratio of the PbI 2 (001) and perovskite (110)  peak intensities increased signicantly with increasing temperature (Fig. 24b). 107This was attributed to the decomposition of the perovskite into PbI 2 at high treatment temperatures, leading to a signicant decline in the performance of PSCs treated at excessively high temperatures.5][226] Addressing this vulnerability in material degradation behavior implies that the durability can be extended by operating the solar device solely in the tetragonal CH 3 NH 3 PbI 3 region (i.e., just below ∼50 °C) or by increasing the phase-transition temperature through feasible lattice engineering. 119A correlation between the intrinsic modication of the perovskite lattice under heating and the interdiffusion of atoms from the boundary material above this thermal threshold is also plausible.It is essential to note that an appropriately timed heat treatment can effectively passivate defects, thereby improving the average PCE of PSCs.
Heat is produced in the PSC under illumination.To elucidate the distinct roles and effects of heat and light in thermal-optical co-processing, changes in device performance under thermal annealing and illumination conditions were investigated (Fig. 25a-c). 227These ndings conrm the synergistic effect of light and heat treatments in improving device performance.The continuous production of photoexcited carriers leads to lattice distortion attributed to polarons/strain. 228,229The strain gradient produced by the resultant driving force accelerates carrier accumulation and remains entirely reversible until the strain-tolerance threshold of the perovskite lattice is reached.However, once the accumulated strain exceeded the straintolerance threshold, lattice damage occurred, resulting in the formation of nanoscale cracks throughout the lm to release excessive strain (Fig. 25d). 111As the strain accumulation process is non-uniform across the polycrystalline perovskite lm, it takes time to achieve the complete release of the internal strain.Therefore, the damaged perovskite lm aer strain relaxation did not exhibit photohalide segregation, offering a plausible explanation for the non-repeatability of polycrystalline MHP lms.In summary, it has been shown that cracks self-heal through heat induction.Defects present in organic-inorganic halide perovskite lms can be addressed through strategies such as passivation using ionic and coordination bonds, use of wide-band-gap materials, and preventing ion migration at extended defects, as depicted in Fig. 11.Semiconductors based on organic-inorganic MHPs adhere to the common ABX 3 perovskite structure, where A can represent either a cation or an inorganic cation, depending on the ion size and Goldschmidt tolerance factor Promising outcomes have been observed with the use of organic cations like MA and formamidine (FA). 1 Adding suitable molecules to perovskites can achieve PSCs with high PCE and thermal stability.For example, the FAPbI 3 perovskite lm degraded quickly aer 18 d of exposure to a humid environment, whereas the FA 0.85 Cs 0.15 PbI 3 lm remained stable aer the addition of Cs. 230 Accordingly, the performance of the FA 0.85 Cs 0.15 PbI 3 device was more stable than that of pure FAPbI 3 cells.Introducing small amounts of Rb + and K + (x # 0.05) to FAPbI 3 can enhance the performance of the PSCs, but higher concentrations may induce phase separation. 158However, PSCs fabricated using a hot-pressing method with a laminated interface for the perovskite lm exhibited suboptimal performance, yielding a PCE of 14.4%. 76,169To obtain large-grain perovskite lms, many researchers have added chloride to the perovskite precursor solution as an effective method for promoting crystallization and grain growth. 231,232For example, MACl containing dimethyl sulfoxide was added to obtain a vertical-oriented perovskite framework with low defect density, thus enhancing the PCE of the resulting PSCs. 233This additive also enhanced grain-boundary movement, facilitating the formation of a dense grain morphology. 4A planar heterojunction PSC with a PCE of 17.10% was achieved by doping PbCl 2 with MAPbI 3 , demonstrating a promising method for the large-scale production of high-performance PSCs through magnetron sputtering. 24xcess PbI 2 in the perovskite lm creates traps that are not conducive to device performance and stability. 24Unlike cations, mixing different halides at the X-position can signicantly inuence the optical and electronic properties, absorption and emission spectra (bandgap), carrier lifetime, and diffusion length. 2 Chlorine doping changes the surface morphology and grain size of perovskite lms by reacting with MAI, which is an effective method for controlling the crystallization of the perovskite phase.A hotpressing technique induced sublimation of the MAI lm, preventing leakage of the MAI vapor. 33Introducing an appropriate amount of PbCl 2 into the perovskite material improves the lm quality by slowing the crystallization rate, resulting in a more uniform, pinhole-free lm, thereby enhancing device performance and stability.However, excess PbCl 2 cannot be fully converted into perovskite by MAI post-processing, resulting in pinholes in the nal perovskite lm. 24Chlorformamidine (FACl) was used as an additive to expand the grain size of perovskite lms and improve their quality. 232The environmental stability of the perovskite lm was signicantly improved; the device maintained 90% of its initial PCE aer 1200 h in ambient air, whereas the original device without FACl treatment maintained only 50% of its initial PCE. 232his approach presents a promising pathway for achieving highperformance and stable PSCs through effective crystallization management.The addition of Cs and FA to perovskite materials can improve the phase stability of CsPbI 3 and inhibit the yellow phase of FAPbI 3 , providing a promising way to improve the PCE and thermal stability.A mixture of large FA and small Cs is conducive to forming the preferred black perovskite phase, removing volatile substances, and improving thermal stability. 234y adding MACl to perovskite materials, a PSC including chloride ions was developed, which achieved a PCE of 21.65% aer 500 h of illumination, a PCE of 96% at 65 °C, and an initial PCE of 85%. 235ACl acts as a crystallization aid to promote grain growth, reduce defects, and form a high-quality perovskite lm with excellent photothermal stability.MABr was incorporated into MAPbI 3 to form a high-quality MAPbI 3−x Br x absorber, and the PCE of the device increased from 14-16% to 19.2%. 161he simultaneous integration of cations and anions leads to notable enhancements in both cell efficiency and stability.For instance, the addition of quaternary ammonium halides to perovskite precursor solutions can simultaneously passivate cation (MA) and anion (iodine) vacancies, with quaternary ammonium compensating for cation vacancies and the halide compensating for anion vacancies. 236BH 4− anions, with a similar radius to that of iodide anions, enable the formation of a stable mixed-halide perovskite structure, MAPbI 3−x (BH 4− ) x , by partially substituting iodide or compensating iodide vacancies.Notably, BH 4− , composed of two elements, exhibits chemical properties akin to halogens, earning it the designation of a superhalogen. 78Fig. 26a shows the effects of additives on the morphology of perovskite lms.Iodine is partially replaced by BH 4− , and all major elements (C, I, N, Pb, and B) are evenly distributed throughout the membrane without obvious phase separation. 78Fig. 26b-d show top-view SEM images of the MAPbI 3 perovskite lm when 0, 5, and 15 mg mL −1 of additives were added. 78For 5 mg mL −1 additive, a smooth, dense, and pinhole-free lm was obtained, whereas concentrations exceeding 10 mg mL −1 resulted in island-like formations, indicating additive accumulation at the grain boundaries.Br doping and the mixing of FA and Cs improved the crystallinity of the crystal, increased the grain size, reduced the trap density and degree of recombination, accelerated the extraction and transfer of charge, and ultimately improved the PCE. 162By selecting or mixing the optimal concentrations of the appropriate ions at the A and X sites, both high PCE and high light stability can be achieved.Strategic modulation of the FA/Cs and Br/I ratios yielded an FA 0.85 Cs 0.15 PbBr 0.15 I 2.85 PSC device that maintained a PCE of 19.6% aer 500 h of light exposure. 237urthermore, a PEAI additive was introduced into a PSC along with Pb(SCN) 2 , which reduced the defect density and energy disorder, improved the carrier mobility and lifetime, and achieved a PCE of up to 19.8% (Fig. 26e). 238This compositional engineering strategy promotes perovskite crystallization, resulting in improved crystal orientation, larger grain sizes, reduced trap densities, and enhanced morphological uniformity.

Passivation-enhanced enhancement
Small organic molecules are widely used materials capable of effectively passivating interfaces in perovskite lms by substantially reducing the number of defects, thereby contributing to the development of efficient and stable PSCs.For instance, Noel et al. demonstrated for the rst time that thiophene can interact with Pb 2+ atoms on the surface of a perovskite, thus passivating defects on the perovskite surface. 239The organic small-molecule pyridyl-2-carboxylead material (PbPyA 2 ) improved the light stability of PSC devices, with an initial PCE of 19.96% and a retention rate of 93% aer 500 h of MPP tracking. 240PbPyA 2 small molecules promote crystallinity, passivate grain boundaries, improve lm quality, and prevent component volatilization.Metal ions and organic cations effectively passivate lms through ionic bonds and other electrostatic interactions with the negatively charged defects in perovskite materials. 241K + passivates the undercoordinated halides at the surface and grain boundaries through ionic interactions, specically with undercoordinated Br − and I − , xing excess halides by forming benign compounds at grain boundaries and surfaces.In addition, K + binding with the halides effectively inhibited ion migration.For example, the addition of potassium iodide to perovskite precursors results in K + accumulating on the surface and grain boundaries, passivating extended defects, and yielding an internal photoluminescent quantum efficiency exceeding 95% in perovskite lms. 242uble-sided passivation layers can greatly increase the V oc and provide signicant stability, 83 that is, the PCBM-PMMA layer on the SnO 2 @TiO 2 layer and the PMMA layer on the perovskite lm.This passivation approach involves the use of a polymer material as both a passivating agent and an insulating component for the perovskite, reinforcing the perovskite lm surface and shielding it from detrimental external degradation factors.Polymer materials are effective surface enhancers for perovskite lms, preventing external degradation.Ligands play an important role in passivating surface defects and/or forming robust bonds with perovskites, thereby protecting the perovskite lattices from degradation.Quantum dots include various elements and ligands and can facilitate surface passivation and interactions with perovskites. 108owever, the practical applications of organic molecular layers are constrained by the presence of inorganic ions and their inherent chemical instabilities.Stable LDPs have proven to be effective in enhancing the interfacial contact between the lightabsorption layer and the HTL. 47,146,243Compared to 3D perovskites, LDPs exhibit a higher formation energy, necessitating more energy for removal.This inhibits the degradation of the perovskite absorbers by protecting them against external factors, thereby improving cell stability. 244urthermore, incorporation of 2D materials can reduce the defect density and ion migration, thereby improving device stability.Triethyl tetramine vapor was used to surface-passivate PSCs, which signicantly improved their PCE (from 17.07% to 18.03%) and stability (PCE retention from 73.4% to 88.9%). 79urthermore, a novel heterocyclic ammonium salt cation (2methylthio-2-imidazoline) was used as a low-dimensional perovskite passivation layer to stabilize the perovskite layer and enhance the photovoltaic performance of PSCs. 87The amphoteric properties and robust molecular interactions of the MT-Im LDP layers effectively passivated the amphoteric Pbbased defects at the interface, substantially inhibiting the generation of Pb 0 .This resulted in a reduction in interfacial nonradiative recombination, an increase in carrier lifetime, and an overall improvement in device stability.These improvements were attributed to the excellent hydrophobicity of MT-Im and its effective targeted treatment of Pb-based defects at the interfaces.
Currently, the further development of PSCs is limited by their high grain-boundary density, interfacial defects, and interfacial energy barriers. 245The introduction of polymers also facilitates defect passivation and performance enhancement.Among the commonly used additives for passivating grain boundaries or surface defects, alkyl ammonium halides stand out because of their ability to passivate both cationic and anionic defects and enhance passivation through hydrogen/ ionic bonds.Son et al. rst reported the precipitation of excess MAI in grain boundaries, where the MAI layer inhibited nonradiative recombination and improved hole and electron extraction in the grain boundaries by forming effective ionconduction pathways. 246Furthermore, BiOBr was grown epitaxially on Cs 2 AgBiBr 6 crystals to inhibit surface defects at the grain boundaries of Cs 2 AgBiBr 6 . 247In Cs 2 AgBiBr 6 , Br vacancies are the main reason for migration (Fig. 27a and b) and the presence of BiOBr provides Br − to ll these vacancies, thus reducing the number of ion migration channels and ion conductivity.In another study, P123 polymer (PEG-PPG-PEG) was added to a perovskite solution and used to functionalize grain boundaries to form a nanoscale grain-boundary wall, which improved the crystallinity of the perovskite and smoothness of the lm. 248Despite their high photostability, these polymers are inherently insulating and hinder the extraction and transfer of charge, thereby limiting potential efficiency gains.
To further reduce the defect density in mixed Sn-Pb perovskites, FSA as a potent reducing molecule can be used to effectively reduce Sn 4+ defects and passivate surface ion vacancies. 249Sulydryl groups react with oxygen molecules to inhibit the oxidation of Sn 2+ , while the O atoms from the sulfhydryl groups act as electron donors and form coordination bonds with the undercoordinated Sn 2+ or Pb 2+ cations, thereby passivating the surface halide vacancies. 250Furthermore, the formamidine groups in FSA, with a cationic structure similar to that of FA, passivate the surface A-site vacancy defects (Fig. 27c). 251This synergistic effect of surface-anchored FSA increased the carrier recombination lifetime in the Sn-Pb perovskite by a factor of three. 251A simple and effective general anionic modication strategy for improving the photovoltaic performance of PSCs was proposed, which involves modifying the perovskite/SnO 2 interface using a series of guanidine salts containing different anions. 245All anions played an active role in passivating SnO 2 and perovskite surface defects, optimizing the interfacial energy band arrangement, and promoting the crystallization of PbI 2 and perovskite.Different modiers exhibited varying degrees of positive effects, which can be netuned by selecting the anion types and interfacial chemical interactions.Interface modication improves the thermal and environmental stability of the perovskite.Cross-linked particles incorporating functional organic molecules have proven to be effective in passivating defects/imperfections on the grain boundaries of perovskite layers.Trimethylpropane triacrylate (TMTA) was incorporated into the MAPbI 3 layer, where the TMTA molecules were chemically anchored to the grain boundaries and crosslinked in situ to form a robust continuous polymer network aer thermal annealing (Fig. 27d). 136The addition of TMTA improved the PCE by passivating defects.Notably, the cross-links formed by the TMTA molecules significantly enhanced the stability of the device against ultraviolet light, temperature, and moisture.The increased PCE was primarily attributed to an increase in the open-circuit voltage.
Techniques for enhancing the PCE of PSCs include the incorporation of additives that simultaneously dope and passivate the materials.For example, the effect of adding MACl to Cs/MA/FA precursor solutions was shown to reduce the nucleation rate and produce strong interconnected lms with larger grains. 235The incorporation of MACl led to a remarkable increase in the grain size from 200 nm to over 1000 nm (Fig. 28a  and b). 235Chloride ions, which are mobile within halide perovskite lms, play a crucial role in crystal formation and growth.The Cl atoms leave the perovskite lattice in the form of MACl, resulting in ion vacancies, particularly on the perovskite surface. 236The surface traps were further reduced by passivation with an isopropyl alcohol iodine solution diluted with chlorobenzene (Fig. 28c). 235The passivation process resulted in an extended carrier lifetime, contributing to a high V oc of approximately 1.24 V, with a minimal potential loss of approximately 370 mV. 235Furthermore, the PSCs exhibited an impressive PCE of 21.65% and robust stability. 235Notably, the distribution of chloride ions within the perovskite layer was non-uniform and predominantly located deep within the layer.It was reported that chlorine was released from the surface of the solar cell aer the formation of the perovskite lm. 135he efficient transfer of photo-excited electrons and holes is crucial for achieving effective solar energy conversion.A simple and effective acid treatment strategy was used to weaken the zigzag octahedral chain bonds in anatase TiO 2 and shorten the crisscrossing octahedral chains, thereby creating an amorphous TiO 2 buffer layer that was tightly bound to the anatase surface and acted as an ETL for efficient electron transport. 252The amorphous TiO 2 ETL had a higher electron density owing to the presence of oxygen vacancies, resulting in the efficient transfer of electrons from the perovskite to TiO 2 .Compared to the asprepared TiO 2 -based devices, the acid-treated PSCs exhibited a higher short-circuit current and PCE.Furthermore, an exceptionally high PCE was achieved for laminated PSCs with the surface and interfacial grain boundaries of the perovskite lms treated with acetonitrile (ACN; a polar aprotic solvent). 76er ACN treatment, the perovskite lm surface became smooth, the grain boundaries dissolved, and the grain boundary interfaces widened.The smooth surface minimizes the probability of local contact between the top and bottom perovskite lms, effectively suppressing hole defects.The hotpressing process enabled uniform elastoplastic deformation of the perovskite lms, resulting in an outstanding PCE of 22.52%.The PSCs exhibited long-term stability, maintaining an average of 96% of their initial PCE for over 2000 h.The composition of the perovskite lms did not change under the applied pressure and heat.In another study, 2,5-diphenyl C 60 fullerpyrrolidine (DPC 60 ) was used as an interface bridge for highly efficient planar PSCs with enhanced stability. 132The hydrophobic DPC 60 layer inhibited the heterogeneous core of the perovskite lms, thereby improving the crystallinity and stability of the device.Compared to PSCs without the hydrophobic DPC 60 layer, the efficiency was 8% higher.Aer 200 h of continuous solar irradiation and thermal aging at 55 ± 5 °C, the devices maintained 82% of their initial PCE.
Introducing quantum dots is another promising approach for developing PSCs with high PCE and thermal stability.
Fluorographene quantum dots (FGQDs) have been used to passivate defects in perovskite lms via the strong interaction between uorine atoms from the FGQGs (with exposed ions and groups) and the perovskite, thereby reducing the trap density, inhibiting non-radiative recombination, and enhancing charge mobility. 48Adding a protective insulation layer to PSC devices is also an effective strategy for enhancing stability as it minimizes the ingress of external degradation factors such as moisture and oxygen.One of the main causes of light and thermal instabilities is ion migration, which alters the chemical composition of perovskites.An effective protective layer plays an important role in inhibiting ion migration and chemical reactions. 108In addition, good protective layers exhibit potent passivation effects, reduce defects, suppress recombination, and facilitate the formation of uniform, highly crystalline, and high-quality lms.Such protective layers have emerged as crucial tools for performance improvement via interfacial engineering, including composition engineering, which is particularly suitable for delicate perovskite materials and other organic/hybrid materials. 108Therefore, to obtain a stable high-performance PCE, it is necessary to both passivate the interfacial defects that inhibit non-radiative recombination and minimize longterm stable ion migration in different environments. 87In summary, a reduction in the unit-cell volume achieved through physical pressure, heating, or component engineering can effectively delay the migration of halides by increasing the activation barrier of the migration process, thereby improving the performance of PSCs.

Structure simulation
Some studies identied or hypothesized that perovskites exhibit intrinsic p-i-n heterojunctions, whereas others have suggested p-p-n or p-n-n + heterojunctions. 207Two possible band diagrams are shown in Fig. 29a (short circuit) and Fig. 29b (open circuit). 32There are no signicant differences under open-circuit conditions, but under a short circuit, the photocurrent generation is quite sensitive to the properties of a few carriers.PSCs are characterized by mixed ion-electron conduction, where the types of ions that can be mobilized are associated with vacancies, ions, or gap defects within the perovskite materials. 204Despite the intrinsic importance of the migration and formation enthalpies in perovskite lms, experimental reports on these aspects are currently lacking.A DFT study of MAPbI 3 at room temperature showed that it contains high concentrations of iodide and MA vacancies. 253Some rstprinciples studies of MAPbI 3 perovskites have shown that the most widely diffused anion is I − (because of its higher mobility), 204,254 suggesting that the migration of Pb and MA vacancies takes a long time.Iodide vacancy migration is the main mechanism of ion migration in perovskites.In addition, ion migration is affected by the inuence of the electric eld distribution on charge collection.
5][256] However, incorporating these thin layers into simulations poses a computational challenge.To address this, previous studies provided models that incorporate the asymptotic expression of the Debye layer charge into a dri-diffusion simulation. 255,257In this model, the exponential voltage drop is associated with the Debye layers, assuming the presence of a constant compensating electric eld between the layers.This model requires further discussion and includes the important feature of charge accumulation at the contact interface, which explains the large capacitance described later.9]191 Diffusion paths along the perovskite crystals were developed to simulate vacancy and defect migration for all four explored defects (Fig. 29c-f). 258The vacancy (V) and gap defects are represented by dotted and red coils, respectively.The dotted line represents the vacancy locus and the solid line represents the migration of ions.Fig. 29c shows the formation of V I at the equatorial position and its migration to the axial position.The V I in the equatorial or axial positions was almost the same.However, the axial position of the V Br was higher than the equatorial position.As shown in Fig. 29d, the inorganic scaffold was responsible for the jump in V MA between adjacent cavities in the ab plane.In addition, V MA diffused within the framework of the Pb 4 I 4 structure.Similarly, Fig. 29e shows the in-plane migration of V Pb along a square formed by four I and four Pb atoms. 208Similar to the V I , the path along the c-axis in Fig. 29f corresponds to MA.In the initial and/or nal conguration, the interstitial I atoms are located between a pair of equatorial and/or axial I atoms of nearly the same length. 258The defects contribute to ion migration, implying that they undergo migration, accumulation, and propagation, resulting in irreversible degradation. 244Therefore, defects are crucial in controlling device stability.
The hidden bottom of the perovskite lm and the beginning of the perovskite lm crystallization are difficult to characterize because of the difficulty in tailoring. 43DFT is a very useful tool in the research and development of PSCs, enabling researchers to gain a deeper understanding and optimize the performance and PCE of such devices.DFT calculations are oen used to simulate the crystallization parameters and electronic properties of perovskites. 18For example, the surface morphology of a 2D perovskite lm aer passivation did not change substantially. 16A DFT study found that the 2D perovskite passivation lm exhibited stronger photoluminescence (PL) emission than that of a control 3D perovskite lm with a longer attenuation life (Fig. 30a-d), owing to the inhibition of nonradiative recombination related to the surface trap state.Furthermore, DFT was used to explore the perovskite phase transition induced by treatment with TETA molecules and predict the potential products in the active and lateral regions of the TETA-treated lms. 79As shown in Fig. 30e, the chemical bonds of Pb-I-Pb were broken aer FA was replaced by TETA molecules, resulting in the separation of the [PbI 6 ] 4− octahedron, and the lattice distortion changed from an orthogonal to a triclinic structure.These results further support the hypothesis that the inclusion of TETA molecules in the crystal structure of the perovskite leads to the transformation of the 3D structure of the perovskite into a quasi-2D material. 144Simulating the electronic structure of perovskite materials aids our understanding of the carriertransport properties of the material, such as the effective masses of electrons and holes and the band structure.This knowledge is crucial for designing more efficient solar-cell materials.
The DFT calculations of the model systems CsPbI 3 and CsPbBr 3 in Fig. 31a show the energy barrier associated with vacancy-assisted halide diffusion. 170The energy barriers of the two materials increased with increasing pressure; when the pressure increased from 0 to 2 GPa, the changes in the energy barriers were 0.134 eV (I) and 0.138 eV (Br), respectively.Although the changes were smaller in the pressure range of 0-0.3 GPa, their impact on migration rates could be signicant owing to the exponential scaling effect.These calculations only considered the effect of pressure on the unit-cell volume in the dark.In practical hybrid materials, the strain also affects the molecular rotational dynamics, distribution of octahedral tilt, and crystal distortion.Muscarella et al. 170 used the denition of the diffusion coefficient to derive the relationship between the segregation rate of ion migration (k seg ) and the effective activation energy: Here, D ‡ S°is the entropy change of a single ion migration step, k B is Boltzmann's constant, n 0 is the attempted frequency of the ion transition, d is the distance of the ion transition, E a is the activation energy, q is the electron charge, 3 pero is the perovskite dielectric constant, 3 0 is the dielectric constant in vacuum, and N is the doping density.The natural logarithm of the migration rate, corresponding to k seg , is proportional to the activation energy of the migration process as follows: Here, −ln(k seg ) is dened as the effective activation energy E * a : According to this denition, the typical activation energy range for halide migration in these perovskites is approximately 100-200 MeV. 259As the pressure applied to all components increased to 0.3 GPa, the experimental E * a increased by a factor of three as a function of the applied physical pressure (Fig. 31b).With increasing annealing temperature, the halide diffusion rate exhibited an Arrhenius relationship, giving E a = 53/28 kJ mol −1 (Fig. 31c and d). 112A higher E a inhibits halide segregation.Photoactivated segregation with low E a enabled the perovskite lms to overcome entropy-driven mixing and produce Br-and Irich domains (Fig. 31e). 172The threshold values were qualitatively consistent with the microscopic model of phase segregation, following a linear temperature-dependent relationship, thus conrming the interaction between heat-driven mixing and light-driven ion segregation of bromide and iodide.
Several mechanisms have been proposed to explain photoinduced halide segregation in mixed-halide perovskites.Initially, a temperature-dependent miscible gap was thought to be the basis of halide segregation.However, this model fails to account for the recovery of mixed phases in the absence of light or restoration of photoinduced halides at low iodine concentrations. 130Another model based on the anti-entropy driving force was later suggested, focusing on the segregation in the energy gap between the uniform and separated iodine-rich  regions. 124Nevertheless, the sign of the driving force appeared to be independent of the optical excitation power and the spatial extent of the excited region.A recent study linked photoinduced halide segregation to the formation of polarons, where the deformation of the ionic perovskite lattice occurs close to the charge carrier. 131In this model, the change in the lattice spacing near the photoexcited carrier serves as the driving force for the separation of different halides.None of these models adequately explains the observed photoinduced halide mixing at high photon uxes, at least in their current formulations.In contrast, Mao et al. developed a lattice model based on the concept of polarization-induced demixing to simulate the variation in halide distribution under broad-range illumination power. 209The model considers three driving forces: (1) the force that attracts I atoms locally owing to the strain gradient generated by the polaron, (2) the force that attracts the carrier/polaron to the I-rich region owing to the reduction (or funnels) in the bandgap, and (3) the force that drives the homogeneous mixing of halides in the absence of a strong strain gradient (Fig. 32a).However, many researchers have proposed that stress-induced strain compensates for photomutagenesis, thereby improving PSC performance.An analytical model was proposed to predict the surface contact between the layers associated with PSC.The deformation of the lm under applied pressure is idealized by modeling the deformation of the cantilever beam around the particle, 260 as follows: where h is the height of the impurity particles, t is the thickness of the top layer (cantilever) under compression deformation, L c is the contact length, L is the cantilever beam length, E is Young's modulus, v is Poisson's ratio, and P is the applied pressure.The results of the surface contact analytical modeling are shown in Fig. 32b and c. 31 For perovskite lms with different thicknesses, the length ratio L c /L increased with increasing P pressure.Thinner lms require less pressure for particle encapsulation, resulting in enhanced interfacial contact around the interlayer particles within thin lms.Furthermore, different cleanroom conditions resulted in different particle sizes, where a reduction in particle size corresponded to an increase in the interfacial contact area.The ndings of the analytical model indicate that higher pressure correlates with enhanced contact between the perovskite active layer and the adjacent layer, thereby improving charge transfer and facilitating the alignment of work functions at the interface.However, excessive pressure may lead to particle sinking 262 potentially damaging the adjacent layers in PSCs.Excessive pressure can also cause the perovskite layer to subside into the adjacent mesoporous layer, eventually leading to short circuits.Consequently, optimal results are achieved with a judicious intermediate pressure, which enhances contact without causing detrimental effects.

Challenges and outlooks
Achieving accurate models and device simulations presents signicant challenges in describing mixed ion-electron conduction.Notably, the PCEs of laminated devices remain considerably lower than those of conventional solar cells.Consequently, future efforts should concentrate on optimizing each component within the device, with a particular focus on overcoming the persistent challenge of excessively high series resistances.This requires careful selection and processing of the ETL, HTL, and additional layers introduced for lamination to minimize the resistance.Despite the high durability of SnO 2 -based laminated structures at elevated temperatures, interfacial reactions can occur in these devices.Developing effective diffusion barriers is expected to be critical for preventing such reactions, enabling a broader selection of structures, including those incorporating more active materials, such as NiO x .In addition, inevitable buried interfaces are present in PSCs, which exhibit a high defect density, adverse strain, low crystallinity, severe ion migration, and harmful voids.Therefore, future research should focus on the fabrication of benign buried interfaces, particularly in the absence of passivation-free methods.For example, ETL materials that better match the perovskite lattice should be developed.
Vapor deposition technology, which is oen overlooked because of equipment requirements, could play a crucial role in advancing PSC industrialization.Currently, PSCs produced by magnetron sputtering exhibit lower efficiencies than those produced by other methods.Exploring the application of vapordeposition technology for industrial-scale PSC fabrication is considered a viable pathway for further development.Although studies on perovskite thin-lm preparation have been conducted, achieving solvent-free, long-term, continuous, and stable deposition remains a challenge.Challenges encountered in the industrial production of devices such as organic lightemitting diodes highlight the need for improved device performance, including optimization of the crystallization process and the identication of structures compatible with solvent-free sputtering processes.
With further developments in composite engineering and the emergence of alternative materials, optimizing ion substitution at two or three sites will undoubtedly result in more stable and efficient PSCs.Given the high sensitivity of MAPbI 3 to electron irradiation, it tends to undergo facile decomposition to form iodide.This degradation process is accompanied by subtle changes in electron diffraction, wherein certain diffraction spots are either missing or weakened, and additional spots may emerge.Consequently, atomicresolution imaging is challenging and oen leads to the misidentication of lead iodide formed aer degradation as a perovskite material.Atomic-resolution imaging is a direct experimental method for visualizing structural defects affecting cell performance, including point and layer defects.However, such imaging tests are challenging with halide perovskites because of their rapid degradation under the microscopy conditions required to achieve sufficient.Therefore, improvements in micro-characterization techniques for perovskite lms are imperative.
Lead-based perovskites are commonly used in PSCs because of their high PCE.Although lead-based perovskites exhibit better photocatalytic hydrogen evolution performance than lead-free perovskite materials, lead toxicity and structural instability are inevitable.These problems have not been completely overcome and are currently hindering the industrialization of PSC devices.To reduce the environmental impact of PSCs and increase their performance, future research should focus on the development of lead-free perovskite materials.

Conclusion
To facilitate the research and development of solvent-free methods for fabricating functional layers in PSCs and the integration of two half-stacks through hot-pressing techniques, this review summarized the recent advancements in the properties and strengthening mechanisms of PSCs.This review provided an overview of the preparation mechanisms involved in solvent-free methods, followed by a comprehensive summary of the PCE, stability, and interfacial morphology requirements.The main enhancement mechanisms in PSCs were systematically classied and summarized, including those based on the composition or concentration of components, pressure, temperature, doping, and passivation.Furthermore, to expedite the overall development and practical applications of PSCs, advanced characterization and simulation techniques were discussed to facilitate a comprehensive understanding of the subject.Finally, the current challenges and future developments in PSCs were discussed.This review provides new insights into improving the efficiency and stability of PSCs.

Fig. 1
Fig. 1 (a) Crystal structure of perovskite.Adapted with permission from ref. 1.Copyright 2015 John Wiley and Sons.Schematic structural representation of MAPbI 3 , where MA = methylammonium in the (b) pseudocubic and (c) tetragonal phases.Adapted with permission from ref. 4. Copyright 2020 American Chemical Society.(d) Dependence of powder X-ray diffraction (XRD) peaks on the value of x in (FAPbI 3 ) 1−- x (MAPbBr 3 ) x single crystals.The hollow circles represent data points, and the solid lines are Gaussian fits of the data.The shift of all the peaks to higher 2q implies contraction of the lattice due to alloying of FAPbI 3 with MAPbBr 3 .Adapted with permission from ref. 2. Copyright 2019 American Chemical Society.(e) Schematic illustration of strain relaxation after MAPBr 3 alloying into FAPbI 3 (side view).Reprinted with permission from ref. 6.Copyright 2016 American Chemical Society.

Fig. 2
Fig. 2 Basic structure of PSCs in (a) regular and (b) inverted configurations.Reprinted with permission from ref. 32.Copyright 2018 John Wiley and Sons.

Fig. 4
Fig. 4 (a) Schematic diagram of the mechanochemical synthesis of perovskite powder by ball milling.Adapted with permission from ref. 53.Copyright 2019 American Chemical Society.(b) The schemes of isostatic pressure process and the compaction kinetics of perovskite powder during the pressing process.Adapted with permission from ref. 59.Copyright 2019 Springer Nature.(c) The perovskite layer preparation process via sputtering. 23,52Adapted with permission from ref. 23.Copyright 2021 John Wiley and Sons and ref. 53.Copyright 2019 American Chemical Society.

Fig. 5
Fig. 5 (a) Crystal growth mechanism of perovskite film during preparation.Adapted with permission from ref. 24.Copyright 2022 American Chemical Society.(b) Schematic of the device structure and fabrication process.(c) Energy band structure of the devices.(d) PCE statistics for sputtering buffer layers with different PMMA : PCBM ratios.Adapted with permission from ref. 22.Copyright 2023 American Chemical Society.
Fig. 7 (a) Common surface defects for perovskites and the effect of various additives.Adapted with permission from ref. 90.Copyright 2020 John Wiley and Sons.(b) Schematic diagram of ACN-treated lamination behavior of layer-perovskite films during hot pressing.Adapted with permission from ref. 76.Copyright 2022 Elsevier.

Fig. 8
Fig. 8 (a) Termination and beginning of the periodic crystal lattice.Adapted with permission from ref. 43.Copyright 2023 Springer Nature.(b) The unit cell structure of a-BaF 2 (left) and g-CsPbI 3 (right).These two planes have a 99.5% lattice matching degree.(c) Cross-section of lattice matched heterostructure between a-BaF 2 and g-CsPbI 3 .(d and e) Structural modeling of the heteroepitaxial growth of g-CsPbI 3 thin film on the a-BaF 2 nanoparticle substrate.Adapted with permission from ref. 96.Copyright 2022 American Chemical Society.

Fig. 9
Fig. 9 (a) 3D schematic diagram of the photoinduced structure change.Adapted with permission from ref. 111.Copyright 2021 American Chemical Society.(b) Reversibility of photoinduced halide segregation.Adapted with permission from ref. 112.Copyright 2020 American Chemical Society.(c) Schematic of photoinduced polaron trapping and associated energy levels.(d) Schematic of macroscale phase segregation with same color key.Adapted with permission from ref. 90.Copyright 2020 John Wiley and Sons.

Fig. 10 (
Fig. 10(a) Schematic to describe the activation of iodine diffusion by oxygen and light.Adapted with permission from ref. 117.Copyright 2019 John Wiley and Sons.(b) Maximum power point tracking (MPPT) results for devices.Adapted with permission from ref. 80.Copyright 2023 Elsevier.(c) Shelf test results of the encapsulated device under 85 °C and 85% RH conditions and (d) long-term operational stability of the encapsulated devices under simulated real operating conditions (maximum power point tracking under 1 sun AM 1.5 G illumination including UV without controlling temperature in ambient air).Adapted with permission from ref. 117.Copyright 2019 John Wiley and Sons.

Fig. 11
Fig. 11 (a) The relationship between the light stability and PCE of PSCs after interface modification of different perovskite layers.Adapted with permission from ref. 108.Copyright 2021 American Chemical Society.(b) These results indicate that the presence of Sn 4+ in the precursor solution leads to the formation of Sn vacancy in the mixed lead-tin perovskite, and the absence of Sn 4+ inhibits the formation of Sn vacancy in tin-reduced precursor perovskite.Adapted with permission from ref. 134.Copyright 2019 Springer Nature.(c) Schematic diagram of the active role of stripped fluorographene quantum dots as passivating agents in perovskite films.Adapted with permission from ref. 48.Copyright 2020 American Chemical Society.(d) Passivation of undercoordinated Pb 2+ on perovskite surface by thiophene or pyridine.Adapted with permission from ref. 91.Copyright 2019 Royal Society of Chemistry.(e) The superhalogen BH 4− aggregates at the iodide ion vacancy, forming a hydrogen bond with methyl ammonium (CH 3 NH 3 + ).Adapted with permission from ref. 78.Copyright 2020 American Chemical Society.

Fig. 12
Fig. 12 Box charts of (a) PCE of optimized TEPA-MAPbI 3−x Cl x and reference MAPbI 3−x Cl x -based devices.Adapted with permission from ref. 139.Copyright 2020 American Chemical Society.(b and c) XRD patterns of the control, unannealed MT-Im (6 mg mL −1 ), and MT-Im (15 mg mL −1 ) perovskite films.(d) PCE distributions for the control and MT-Im perovskite devices.(e) Schematic illustration of the effective management by inherently stable MT-Im LDP for the Pb-based defects at the interface.Adapted with permission from ref. 87.Copyright 2020 American Chemical Society.

Fig. 14 (
Fig. 14 (a) Variation of the PCE at damp-heat test of encapsulated devices.(b) Continuous MPP tracking for the encapsulated control and 2D-RT cells under AM 1.5 illumination in ambient air.2D-RT: 2Dperovskite layers when post-treatment was performed at room temperature.Adapted with permission from ref. 16.Copyright 2022 The American Association for the Advancement of Science.(c) Longterm stability test result for the PSCs fabricated with control and Brrich perovskite film, conducted at MPP bias under continuous AM 1.5 G illumination.Adapted with permission from ref. 162.Copyright 2019 John Wiley and Sons.(d) Using large cations to adjust the dimension.Adapted with permission from ref. 167.Copyright 2018 The American Association for the Advancement of Science.

Fig. 15
Fig. 15 Different hot pressing methods.Adapted with permission from ref. 28.Copyright 2023 American Chemical Society.Adapted with permission from ref. 30.Copyright 2019 American Chemical Society.Adapted with permission from ref. 33.Copyright 2021 John Wiley and Sons.Adapted with permission from ref. 76.Copyright 2022 Elsevier.Adapted with permission from ref. 101.Copyright 2018 American Chemical Society.Adapted with permission from ref. 103.Copyright 2022 American Chemical Society.Adapted with permission from ref. 168.Copyright 2019 American Chemical Society.Adapted with permission from ref. 169.Copyright 2020 John Wiley and Sons.

Fig. 16 (
Fig. 16 (a) Comparison of iodine-related defect properties in MAPbI 3 to micro-structural characteristics as function of stoichiometry.Adapted with permission from ref. 175.Copyright 2022 American Chemical Society.(b) Surface X-ray photoelectron spectroscopy (XPS) of the CsPbBr 3 film.(c) Energy disperse spectroscopy (EDS) fit curve to show the relative percentage of atoms.Adapted with permission from ref. 21.Copyright 2021 AIP Publishing.(d) Evolution curves of band gap for triple-halide films with increased ratio of Cl/(I + Br + Cl).(e) Evolution curves of host perovskite lattice constant with increasing ratios of Cl/(I + Br + Cl).Adapted with permission from ref. 185.Copyright 2020 The American Association for the Advancement of Science.

Fig. 18
Fig. 18 (a) Post heat pressing-treated samples with RMS values.Adapted with permission from ref. 103.Copyright 2022 American Chemical Society.(b) Statistical distribution of domain grain size.Adapted with permission from ref. 33.Copyright 2021 John Wiley and Sons.(c) Schematics of the interfacial surface contact.Adapted with permission from ref. 31.Copyright 2020 Springer Nature.

Fig. 19 (
Fig. 19 (a) Solid-state in-plane growth-processed 2D/3D films after 10 min at (a) 20 MPa, (b) 40 MPa and (c) 60 MPa.Adapted with permission from ref. 75.Copyright 2021 Springer Nature.(d) Schematic representation of the suppression of segregation by compressing the mixed-halide perovskite.Adapted with permission from ref. 172.Copyright 2020 Elsevier.(e) XRD patterns before and after pressure application.(f-h) Scanning electron microscope (SEM) images of pressure-assisted perovskite films.Adapted with permission from ref. 31.Copyright 2020 Springer Nature.(i) Schematic illustration of phase segregation originated from grain boundaries of the control sample and (j) constrained mobile defects at the grain boundary for the post heat pressing-treated sample.Adapted with permission from ref. 103.Copyright 2022 American Chemical Society.

Fig. 20
Fig. 20 Mechanism scheme of phase segregation stabilization by external physical pressure: high pressure increases the activation energy of halide migration, high-pressure suppression of phase segregation.Adapted with permission from ref. 170.Copyright 2020 American Chemical Society.

Fig. 21 (
Fig. 21 (a) Absorbance spectra of layers.Adapted with permission from ref. 200.Copyright 2016 American Chemical Society.Crosssectional SEM images of MAPbI 3 /TMTA thick films: (b) with softpressing (the scale bar is 100 mm) and (c) without pressing (the scale bar is 300 mm).Surface SEM of MAPbI 3 /TMTA thick films (d) with softpressing and (e) without pressing.Adapted with permission from ref. 42.Copyright 2022 John Wiley and Sons.(f) Schematic diagram of active area in charge extraction by columnar and continuous perovskite structure.Adapted with permission from ref. 200.Copyright 2016 American Chemical Society.

Fig. 22
Fig. 22 SEM images for (a) the control perovskite film annealed under normal conditions and (b) the target perovskite film annealed under saturated MAI vapor.The perovskite film prepared by the gas flowinduced gas pump method; "target" represents the perovskite film with PbCl 2 additive treated by the HPS method.Adapted with permission from ref. 33.Copyright 2021 John Wiley and Sons.(c) The SEM images of the films grown under different substrate temperatures, 50-250 °C.Scale bar: 1 mm.Adapted with permission from ref. 21.Copyright 2021 AIP Publishing.(d-i) Field emission scanning electron microscopy (FE-SEM) plane-view images of control and post heat pressing-treated MHP.Adapted with permission from ref. 103.Copyright 2022 American Chemical Society.

Fig. 23 (
Fig. 23 (a) AFM images of delaminated perovskite surfaces.Adapted with permission from ref. 169.Copyright 2020 John Wiley and Sons.(b) I exc, threshold as a function of temperature for observing halide ion segregation in MAPbBr 1.5 I 1.5 mixed halide perovskite films.Adapted with permission from ref. 112.Copyright 2020 American Chemical Society.(c) Annealing temperatures of different hybrid and inorganic perovskite films during formation.(d) Schematic showing the formation of tensile and compressive strains.Adapted with permission from ref. 176.Copyright 2020 Springer Nature.(e) Diagram of enthalpy driven separation process and entropy driven remixing process.Adapted with permission from ref. 172.Copyright 2020 Elsevier.

Fig. 24 (
Fig. 24 (a) FWHM, peak positions, and intensities of the curves.(b) Peak intensity ratio and average crystallite size of the curves.Adapted with permission from ref. 107.Copyright 2020 Springer Nature.(c) Scheme of the rotational state for the MA + at different temperatures.Adapted with permission from ref. 119.Copyright 2018 American Chemical Society.

Fig. 25
Fig. 25 Influence of thermal-annealing temperature on the device performance of quasi-2D PSCs (a) in the dark and (b) light conditions.(c) Influence of light intensity on the performance of quasi-2D PSCs.Adapted with permission from ref. 227.Copyright 2018 American Chemical Society.(d) SEM images and corresponding schematic diagram of strain accumulating/releasing induced photoinduced halide segregation/photoinduced self-healing procedures.Adapted with permission from ref. 111.Copyright 2021 American Chemical Society.

Fig. 27 (
Fig. 27 (a) Schematic diagram of BiOBr passivation inhibiting ion migration.Adapted with permission from ref. 59.Copyright 2019 Springer Nature.(b) Schematic cross-section of a film showing halide vacancy management in the case of excess halide.Adapted with permission from ref. 242.Copyright 2018 Springer Nature.(c) Schematic illustration of suppressing Sn 2+ oxidation and the passivation of halide and cation vacancy at the grain surface of mixed Sn-Pb perovskite films enabled by FSA molecule.A-Site represents the organic monovalent cations in the lattice.Adapted with permission from ref. 251.Copyright 2021 Springer Nature.(d) Cross-linking mechanism using TMTA molecules.Adapted with permission from ref. 136.Copyright 2018 Springer Nature.

Fig. 28
Fig. 28 Top-view SEM images of triple A-cation perovskite films (a) without and (b) with MACl additive in the starting solution.(c) Schematics of the triple A-cation perovskite films without MACl, with MACl additive and after passivation with iodine.Adapted with permission from ref. 235.Copyright 2018 John Wiley and Sons.

Fig. 29
Fig. 29 General energy band diagram in short circuit (a) and open circuit (b) for different possible perovskite conductivities, as indicated, being E F the equilibrium Fermi lever and E Fn and E Fp the quasi Fermi Levels for electrons and holes, respectively.Reprinted with permission from ref. 32.Copyright 2018 John Wiley and Sons.Pathway for migration of vacancies and defects: iodine (c), methylammonium (d), lead (e) and iodine defects (f).Reprinted with permission from ref. 258.Copyright 2015 RSC Publishing.

Fig. 30
Fig. 30 Density functional theory results: (a) relaxed structure, (b) charge density difference, and (c) partial densities of states for an oleylammonium molecule on the PbI 2− terminated (001) surface of FAPbI 3 .(d) Partial densities of states of the pristine PbI 2− terminated (001) surface of FAPbI 3 .Adapted with permission from ref. 16.Copyright 2022 The American Association for the Advancement of Science.(e) The optimal lattice structures of FAPbI 3 , (TETA)(FA)Pb 2 I 6 and (TETA) PbI 3 were analyzed by DFT.Adapted with permission from ref. 79.Copyright 2020 American Chemical Society.

Fig. 31 (
Fig. 31 (a) Calculated activation energy for iodide and bromide diffusion in CsPbI 3 and CsPbBr 3 as a function of unit cell volume.(b) −ln(k seg ), which is proportional to the activation energy for phase segregation, plotted against the external physical pressure applied for x = 0.5 and x = 0.7.Adapted with permission from ref. 170.Copyright 2020 American Chemical Society.Arrhenius diagram with MAPbBr 1.5 I 1.5 mixed halide perovskite rate constant inversely proportional to temperature: (c) initial complete separation position, (d) under constant light exposure.Adapted with permission from ref. 112.Copyright 2020 American Chemical Society.(e) The relationship between halide segregation and remixing with energy, pressure, temperature, and light duration.Adapted with permission from ref. 172.Copyright 2020 Elsevier.

Fig. 32 (
Fig. 32 (a) Illustration of halide ion distribution for a MAPb(Br 0.8 I 0.2 ) 3 perovskite lattice in response to low carrier density (left) and high carrier density (right).Adapted with permission from ref. 209.Copyright 2020 Springer Nature.Analytical model prediction of pressure effects on contact length ratios: (b) effects of pressure on the surface contacts for different thicknesses of the films (for particle size of 1 mm) and (c) effects of pressure on surface contacts for different sizes of the particles (for a film thickness of 250 nm).Adapted with permission from ref. 31.Copyright 2020 Springer Nature.

Table 1
Different functional layers and properties of PSCs a